Fn, 68.37.Hk, 68.55.Jk, 81.15.Ef Cu(In,Ga) (S,Se) 2 thin films were fabricated by sequential evaporation from CuGaSe 2 , CuInSe 2 and In 2 S 3 compounds for photovoltaic device applications. From XRF analysis, the Cu : (In + Ga) : (S + Se) atomic ratio in all thin films was approximately 1 : 1 : 2. As the [In 2 S 3 ]/([CuGaSe 2 ] + [CuInSe 2 ]) mole ratio in the evaporating materials increased, the S/(S + Se) atomic ratio in the thin films increased from 0 to 0.16 determined by XRF and to 0.43 by EPMA. XRD studies demonstrated that the prepared thin films had a chalcopyrite Cu(In,Ga) (S,Se) 2 structure and the preferred orientation to the 112 plane. The SEM images demonstrated that Cu(In,Ga) (S,Se) 2 thin films had large and columnar grains.

Poly-p-xylylene films have been utilized as protective and barrier layers for gases and solvents on electronic and implantable devices. Here we report a new approach to create highly permeable and selective nanofiltration membranes coated with microporous poly-p-xylylene nanofilms fabricated through a dry chemical vapor deposition process by using [2.2]paracyclophanes derivatives on ultrafiltration membranes. The introduction of crosslinking points into rigid poly-p-xylylenes enhanced microporosity and mechanical strength due to insufficient packing and depression of structural relaxation among polymer chains in three-dimensional networks. Crosslinked nanofilms with thicknesses down to 50 nm showed outstanding permeability for water and alcohols at a pressure difference of 0.5 MPa and exhibited higher rejection ratios for water-soluble organic dyes than non-crosslinked nanofilms. Poly-p-xylylene nanofilms also showed an excellent blocking property for non-polar organic solvent permeation through specific interaction of hydrophilic pores with organic solvents.