This study compared 3 composites made of hydroxyapatite and polyhydroxybutyrate to determine their biocompatibility, osteointegration, and osteoconduction in rabbits bone defects. Hydroxyapatite-polyhydroxybutyrate was tested in a 10:90 vol/vol ratio for composite 1, 25:75 for composite 2, and 50:50 for composite 3, whereas defects in the control group remained unfilled. Limbs were clinically and radiographically evaluated, and samples were taken 8, 45, and 90 days after surgery for histologic and histomorphometrical analysis. No significant difference was found in the clinical parameters: pain, lameness, dehiscence, infection, and edema among the 4 groups. No signs of osteolysis or periosteal reaction were observed. Bone regeneration in groups 1, 2, and 3 occurred histomorphologically similar to the control group. No inflammatory infiltrate was present on any date of observation. More bone than connective tissue was significantly found in the defects of the 3 groups on all observation dates, and the percentage of bone tissue in the interface was similar for composites 2 and 3. Bone and connective tissue were observed in pores of composites 2 and 3. Osteoclasts were found in the bone-composite interface, and multinucleated giant cells were seen on the surface of composite fragments, found among mesenchymal tissue on the 45th and 90th days. No significant difference was observed in osteoclast number among the 4 groups. In summary, composites were considered biocompatible and able to integrate to bone. They also showed signs of biodegradability, and composites 2 and 3 were osteoconductive, the first displaying best characteristics for bone substitution.
295Pesq. Vet. Bras. 30(4):295-300, abril 2010 RESUMO.-No presente estudo foi avaliada a arquitetura tecidual, a população celular, assim como a integridade e a distribuição dos tipos celulares em meniscos frescos de coelhos e preservados em glicerina 98%. Foram analisados meniscos mediais de coelhos recém abatidos, que foram distribuídos em três grupos: o grupo MF (n=7), composto por meniscos frescos, correspondeu ao grupo controle; o grupo MG (n=7), composto por meniscos preservados em glicerina 98%, por 30 dias, e o grupo MR (n=7), por meniscos preservados em glicerina 98% e reidratados em NaCl 0,9%, por 12 horas. Em todos os meniscos foram identificados e quantificados os diferentes tipos celulares: fibroblastos/fibrócitos e condrócitos. A população celular foi estatisticamente semelhante nos três grupos de meniscos, sendo que os meniscos preservados, grupos MG e MR, apresentaram menor intensidade de coloração e retração das fibras colágenas, diminuição de volume e maior intensidade de coloração dos núcleos (condensação da cromatina), em relação aos meniscos frescos (MF), caracterizando o fenômeno de lise celular. In the present study was evaluated the tissue architecture, the percentage of cellular population, as well as viability and distribution of cells in fresh menisci of rabbits and preserved in 98% glycerin. Were analyzed medial menisci of rabbits freshly slaughtered, which were distributed into three groups: the MF group (n=7), composed of fresh menisci, corresponded to the control group; the MG group (n=7), composed by menisci preserved in 98% glycerin, for 30 days, and the MR group (n=7) by menisci preserved in 98% glycerin and rehydrated in NaCl 0.9% for 12 hours. In all menisci were identified and quantified the different cell types: fibroblasts/fibrocytes and condrocytes. The cell population percentage was statistically similar in all groups. All menisci preserved in the MG and MR groups showed a lower intensity of color and shrinkage of collagen fibers, reduced volume and higher intensity of staining of nucleus (chromatin condensation), as compared to fresh menisci (MF), featuring the phenomenon of cell lysis. The cartilaginous matrix of preserved menisci proved to be well preserved because the tissue architecture was maintained. It was concluded that 98% glycerin is an optional preservation mean for meniscal allografts with a devitalized collagenous matrix.INDEX TERMS: Articular cartilage, meniscal allograft, knee.
RESUMOAvaliaram-se a biocompatibilidade, a osseointegração, a osseocondução e a biodegradação de compósitos de 50% hidroxiapatita (HAP-91®) e 50% poli-hidroxibutirato. O compósito foi implantado em defeitos ósseos em 12 coelhos (grupo experimental), sendo comparado a defeitos não preenchidos (grupo-controle, de igual número). Os parâmetros clínicos dor, claudicação, infecção, deiscência e edema foram avaliados nos primeiros oito dias após a cirurgia e aos 45 e 90 dias. Radiografias foram realizadas aos oito, 45 e 90 dias após a cirurgia em quatro animais por grupo que, em seguida, foram submetidos à eutanásia para coleta de amostras destinadas a análises histológica e histomorfométrica. Não ocorreram diferenças entre os grupos para todos os parâmetros clínicos. Radiografias demonstraram um compósito com radiopacidade semelhante à do osso vizinho e contato direto entre osso e compósito aos 45 e 90 dias. Diferença significativa foi observada entre a porcentagem dos tecidos ósseo e conjuntivo dentro do defeito nos dias oito, 45 e 90, assim como na interface aos 45 e 90 dias. Foram observadas projeções dos tecidos ósseo e conjuntivo no interior do compósito e sinais de biodegradação na ausência de infiltrado inflamatório. Pode-se concluir que o compósito é biocompatível, osseocondutor, biodegradável e se integra ao tecido ósseo.
RESUMOPara avaliar o compósito hidroxiapatita-lignina na osseointegração entre implante metálico e o tecido ósseo, foram utilizados 20 coelhos adultos, nos quais foi realizada uma falha óssea na face lateral proximal de ambas as tíbias. Na tíbia esquerda, introduziu-se, no canal medular, um pino intramedular de Schanz revestido com o compósito em sua parte rosqueada, após o preenchimento daquele com 1000mg do compósito. A falha cortical foi preenchida com o compósito. O mesmo foi feito na tíbia direita, porém sem a utilização do compósito, servindo como controle. A avaliação clínica baseou-se na deiscência, claudicação, sensibilidade dolorosa e circunferência tibial. Foram realizadas radiografias imediatamente após a cirurgia e aos oito, 30, 60, 90 e 120 dias do pós-operatório. A maioria dos animais apresentou evolução clínica normal. Nas radiografias do grupo tratado, houve decréscimo da radiopacidade no defeito e no espaço medular até tornar-se semelhante à do osso circunvizinho, quadro inverso ao do grupo-controle. Conclui-se que o compósito hidroxiapatita-lignina não mostrou indícios clínicos de rejeição e que o tecido visualizado na altura da falha óssea e ao redor do pino intramedular tinha radiopacidade semelhante à do osso circunvizinho, o que sugere que o material promoveu a integração com o tecido ósseo.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.