Despite being exposed to the harsh sea-spray environment of the North Sea at Arbroath, Scotland, for over 63 years, many of the reinforced concrete precast beam elements of the 1 . 5 km long promenade railing are still in very good condition and show little evidence of reinforcement corrosion. In contrast, railing replacements constructed in about 1968 and in 1993 are almost all badly cracked as a result of extensive corrosion of the longitudinal reinforcement. This is despite the newer concrete appearing to be of better quality than the 1943 concrete. Statistics for maximum crack width for each of the three populations, based on measurements made in 2004 and in 2006, are presented. In situ and laboratory measurements show that the 1943 concrete appears to have high permeability but it also shows high electrical resistivity. Chloride penetration measurements show the 1943 and 1993 concretes to have similar chloride profiles and similar chloride concentrations at the reinforcement bars. This is inconsistent with the 1943 beams showing much less reinforcement corrosion than their later replacements and casts doubt on the conventional practice for durability design focusing on reducing concrete permeability through denser concretes or greater cover.

No abstract

Abstract. An attempt has been made to purify factors present in aqueous extracts of pig epidermis which inhibit epidermal cell proliferation. A lipophilic factor of low molecular weight (less than 10,000), has been shown to inhibit DNA synthesis as measured by the uptake of tritiated thymidine in mouse ear epidermis. Purification by alcohol precipitation, ethyl acetate extraction and silicic acid column chromatography produced a fifteen‐fold increase in the specific activity of the inhibitory action. It seems likely that aggregation or absorption of this low molecular weight factor may explain the high molecular weight of epidermal cell proliferation inhibitors previously studied, as well as the difficulty in their characterization.