This study evaluated the bond strength (BS) and the adhesive interface of four endodontic sealers to root canal dentine, before, and after immersion in phosphate buffered saline (PBS) to simulate an in vivo environment. Eighty roots were instrumented using ProTaper rotatory files, under irrigation with 17% EDTA and 1% NaOCl. Posteriorly were divided into four groups (n = 20) according to the sealer used: Endofill, AH Plus, Sealapex, and MTA Fillapex. Each group was divided into two subgroups (n = 10) and stored at 37°C immersed in water for 7 days and in PBS for 60 days. From each subgroup, 1 mm thick sections were obtained. One section of each region (coronal, middle, and apical) was submitted to the push-out test and failures were observed. Twelve sections of each subgroup (four from each region) were evaluated under SEM. Three-way ANOVA evaluation for BS showed significant differences between groups and regions (P < 0.0001), but not between subgroups (P > 0.05). AH Plus had significantly higher BS than the others sealers, regardless of the analyzed subgroup (Tukey's test, P < 0.5). The most common failures were adhesive to dentine and cohesive of the sealer. The SEM evaluation (Kruskal-Wallis, Mann-Whitney) showed homogeneous adhesive interface formed and sealer tags in all groups with significant statistical differences with AH Plus, regardless of PBS immersion. AH Plus was superior to the other sealers for both BS and quality of interface formation. Immersion in PBS did not interfere on BS or adhesive interface of the sealers tested.

A proper interface formed between sealer and dentine is very important for final quality of root canal filling. Observational methods which allow an accurate analysis of this interface must be selected to assess such features.

This study correlated the bond strength (BS) and dentin penetration of different sealers by push-out test and Confocal Laser Scanning Microscopy (CLSM) analysis. Forty-five root canals were prepared according to the crown-down technique and filled with gutta-percha associated to the following sealers (n=15): Endofill, AH Plus and MTA Fillapex. Five canals of each group were filled with the sealers added with 0.1% Rhodamine B dye. Next, the specimens were transversely sectioned and submitted to the push-out test (n=10) and CLSM analysis (n=5). The BS data showed the following means (MPa) and standard deviation: AH Plus (4.17±1.86); MTA Fillapex (3.13±1.96) and Endofill (2.10±1.03). Statistical analysis (two-way ANOVA, α=0.05) showed significant difference among sealers (p<0.001) and root canal thirds (p<0.001). The BS results of Endofill and MTA Fillapex were statistically similar (p>0.05), however, they were statistically different from AH Plus (p<0.001). The regional analysis of BS showed similarity between middle and apical thirds (p>0.05), and both were different from coronal portion (p<0.001). CLSM analysis verified tags formation in all groups and higher penetration of the specimens filled with AH Plus (p<0.05). The Kendall test (correlation between BS to dentin and sealer penetration into dentinal tubules) and the Pearson test (between failures pattern and sealer penetration into dentinal tubules) did not show correlation between the variables evaluated for all the tested sealers (p>0.05). AH Plus group had higher BS to dentin, and deeper tags formation than the other sealers. There was no significant correlation between BS and intratubular penetration of the tested sealers.

The aim of this study was to assess the effects of intracanal irrigation with sodium hypochlorite (NaOCl) and ethylenediaminetetracetic acid (EDTA) prior to calcium hydroxide medication on the compressive strength of root dentin. Forty-eight roots with single and straight canals were instrumented with a crown-down technique using Flexofile files and Gates Glidden burs, under 0.9% sodium chloride (NaCl) irrigation. Root canals were randomly separated into 4 groups (n=12), according to the irrigating solution: Control Group, 0.9% NaCl; Group NaOCl , 1% NaOCl; Group EDTA , 17% EDTA; and Group EDTA+NaOCl , 17% EDTA and 1% NaOCl. Solutions remained for 40 min, renewed every 10 min, except for Group EDTA+NaOCl , where the solutions were alternated every 10 min. Canals were dried and filled with calcium hydroxide paste, and radiographed. Each canal was sealed and stored at 37 °C for 30 days. After this period, the roots were cut 1 mm below the cementoenamel junction and 6 mm apically from this point in order to obtain 6 mm-long cylinders. The compressive test was conducted with a crosshead speed of 1 mm/min. The means (±SD) (MPa) of compressive strength were: Control Group, 151.23±94.36; Group NaOCl , 167.50±57.25; Group EDTA , 108.79±99.88; Group EDTA+NaOCl , 60.12±92.10. Significant statistical differences among groups were found (ANOVA and Tukey, α=5%, p=0.02). Control Group and Group NaOCl showed higher means of compressive strength than Group EDTA+NaOCl . Intracanal irrigation with 17% EDTA and 1% NaOCl produced a significant reduction of dentin compressive strength 30 days after medication with calcium hydroxide.

No abstract