No abstract

No abstract

The biphasic calcium phosphate (BCP) concept was introduced to overcome disadvantages of single phase biomaterials. Different composition ratios of BCP bioceramics have been studied, yet controversies regarding the effects of ratio on biomaterial behavior still exist. In this study, BCP scaffolds were prepared from nano hydroxyapatite (HA) and β-tricalcium phosphate (β-TCP) that were synthesized via a solid state reaction. Three different composition ratios of pure BCP and collagen-based BCP scaffolds (%HA/%β-TCP; 30/70, 40/60, and 50/50) were produced using a polymeric sponge method. Physical and mechanical properties of all materials and scaffolds were investigated. SEM showed overall distribution of both macropores (80-200 μm) and micropores (0.5-2 μm) with high interconnected porosities. Total porosity of pure BCP (90% ± 3%) was found to be higher than collagen-based BCP (85% ± 2%). It was observed that following sintering process, dimensional shrinkage of large scaffolds (39% ± 4%) was lower than small ones (42% ± 5%) and scaffolds with high HA ratios (50%) experienced higher dimensional changes than those with higher β-TCP (70%) ratios (45% ± 3% and 36% ± 1%, respectively). Compressive strength of both groups was less than 0.1 MPa and collagen coating had almost no influence on mechanical behavior. Further studies may improve the physical properties of these scaffolds and investigate their exact biological behaviors.

The purpose of this study was to investigate liver and intestinal ABCA1 expression and plasma HDL-C level in response to treadmill-running training in rats. Twenty adult Wistar male rats (17-18 weeks old, 300-322 g) were divided into control (n = 10) and Training (n = 10) groups. Training group trained at 25 m/min (0% grade) for 60 min/day, 5 days/week for 12 weeks. Rats were killed 48 h after the last session of training. The intestinal and liver ABCA1 mRNA expression was found to be significantly higher in trained compared to control group (P < 0.006 and P < 0.024, respectively). Intestine and liver ATP concentrations remained unchanged. Plasma HDL-C, HDL2-C, Apo A-1, pre-beta HDL-C concentration, LCAT activity, TC/HDL-C and LDL-C/HDL-C ratio significantly increased in trained group (P < 0.01, P < 0.006, P < 0.001, P < 0.001 P < 0.067, P < 0.02, and P < 0.03, respectively). However, other lipoprotein concentrations were unchanged. In conclusion, we found that endurance training induced significant elevation in plasma HDL-C and HDL2-C concentrations, accompanied by higher plasma Apo A-1, pre-beta HDL-C concentrations, LCAT activity and ABCA1 mRNA expressions in rat intestine, and liver.

The data presented in this article are related to the research article entitled “Biphasic calcium phosphates bioceramics (HA/TCP): Concept, physicochemical properties and the impact of standardization of study protocols in biomaterials research” [1]. This article provides in depth study of BCP bone substitutes as valuable option in the field of tissue engineering. However, there are discrepancies in the literature regarding the ideal physicochemical properties of BCP and the ideal balance between different phase compositions for enhanced bone tissue engineering (M. Ebrahimi, M.G. Botelho, S.V. Dorozhkin, 2016; M. Ebrahimi, P. Pripatnanont, S. Suttapreyasri, N. Monmaturapoj, 2014) [1,2]. This is found to be mainly because of improper characterization of BCP bioceramics in basic studies and lack of standard study protocols in in vitro and in vivo research. This data article along with original article provide the basic data required for ideal characterization of BCP and other bioceramics in an attempt to provide basic standardized protocols for future studies.