The smallest changes of hardness and roughness with time in the modified groups compared to controls were observed for itraconazole groups for both materials.

No abstract

albicans biofilm on the hardness and roughness of temporary denture soft liners. Specimens (n=8; 36×7×6 mm) of tissue conditioner (Softone) and resilient liner (Trusoft) were produced either without (control) or with incorporation of drugs at MICs: nystatin (0.032 g/mL), chlorhexidine diacetate (0.064 g/mL), ketoconazole (0.128 g/mL), miconazole (0.256 g/mL) and itraconazole (0.256 g/mL). Specimens were stored in distilled water at 37 °C for 24 h, 7 days and 14 days prior to the hardness/roughness measurements. Data were analyzed by 3-way ANOVA and Tukey HSD test (α=0.05). The addition of the antifungals into both materials demonstrated no evident hardness change or decrease of this property compared with the control, except for miconazole in Softone, which increased the hardness after 14 days (p=0.003). The addition of nystatin into both materials, chlorhexidine in Trusoft and ketoconazole in Softone resulted in no significant changes of roughness compared with the control, after 7 days and 14 days (p>0.05). In these periods, itraconazole increased the roughness of both materials (p<0.001). The addition of all antifungals, except for the miconazole in Softone, resulted in no deleterious effects on the materials' hardness over the evaluation time. The MICs of nystatin in both temporary soft lining materials, ketoconazole in Softone and chlorhexidine in Trusoft resulted in no deleterious effects for roughness up to 14 days.

This study evaluated the influence of zirconia surface finishes on the wear of an enamel analogue. 40 zirconia discs were divided into four groups: control (without finish); glazed; polished; polished and glazed. All samples were subjected to wear against steatite antagonists. The specimens underwent roughness, topographic, scanning electron microscopy (SEM) and wettability analyses. Quantitative wear measurements were performed on both steatites and discs. To measure wear of steatites the weight before and after the test and the diameter after the test were used. Profilometer measurements were performed to determine the wear on discs. Roughness, volumetric wear and mass loss were analyzed using the Kruskal-Wallis and Dunn tests (5%), while contact angle values were analyzed with One-way ANOVA and Tukey tests (5%). The polished group had the lowest roughness means, being statistically different from the other groups (p-value=0.0001). The glazed group presented the lowest steatite volumetric wear (p-value=0.0001), but not statistically different from the polished and glazed group, whereas these groups presented the highest zirconia volumetric wear, with statistically different (p-value=0.0002) compared to the others. SEM showed irregularities on the control groups surface, grooves on the polished group, and a homogeneous surface for the glazed group with a few pores. All groups presented contact angles lower than 90 degrees, characterizing hydrophilic surfaces. It can be concluded that just glazed zirconia caused less wear on the antagonist when compared to no finish and polished zirconia.

Background: The aim of this study was to evaluate the preventive effect in vitro of experimental gel containing iron and ⁄ or fluoride on the erosion of bovine enamel. Methods: To standardize the blocks (n = 80), specimens (4 · 4 mm) were previously selected to measure the initial microhardness. The blocks were randomly allocated into four groups of 20 samples each: C (control, placebo gel); F (fluoride gel, 1.23% NaF); Fe (iron gel, 10 mmol ⁄ L FeSO 4 ) and F + Fe (fluoride + iron gel). The gels were applied and removed after 1 minute. The blocks were then submitted to six alternating remineralization and demineralization cycles. The beverage Coca-Cola Ò (10 minutes, 30 mL) was used for demineralization, and artificial saliva (1 hour) for remineralization. The effect of erosion was measured by wear analysis (profilometry). Data were analysed by ANOVA and the Tukey test for individual comparisons (p <0.05). Results: The mean wear (± SD, lm) was C: 0.94 ± 0.22; F: 0.55 ± 0.12; Fe: 0.49 ± 0.11 and F + Fe: 0.55 ± 0.13. When the experimental gels were used, there was statistically significant reduction in enamel wear in comparison with the control (p <0.001). However, the experimental gels did not differ significantly among them. Conclusions: The gels containing iron with or without fluoride are capable of interfering with the dissolution dental enamel in the presence of erosive challenge.