In this work the in vitro antimicrobial activity of colloidal solutions of nine different commercially available nanoparticles were investigated against Staphylococcus aureus strains, both methicillin-sensitive (MSSA) and methicillin-resistant (MRSA). Research covered antimicrobial investigation of different metal and metal-oxide nanoparticles, including Ag 10 nm, Ag 40 nm, Al2O3 100 nm, Au 20 nm, Pt 4 nm, TiO2 100 nm, Y2O3 100 nm, ZnO 100 nm and ZrO2 100 nm nanoparticles. Such materials were foreseen to be applied as coatings on 3D-printed biodegradable polymers: i.e., catheters, disposable materials, hospital bedding items, disposable antimicrobial linings and bandages for chronic wounds. Therefore, the antimicrobial activity of the nanoparticles was determined by agar well diffusion assays and serial microdilution broth assays. In addition, the chromatographic characterization of elements present in trace amounts was performed as a method for tracing the nanoparticles. Moreover, the potential of preparing the rough surface of biodegradable polymers for coating with antimicrobial nanoparticles was tested by 3D-printing fused deposition methodology. The in vitro results have shown that particular nanoparticles provided powerful antimicrobial effects against MSSA and MRSA strains, and can be easily applied on different biopolymers.

The development of antimicrobial polymers is a priority for engineers fighting microbial resistant strains. Silver ions and silver nanoparticles can assist in enhancing the antimicrobial properties of microcapsules that release such substances in time which prolongs the efficiency of antimicrobial effects. Therefore, this study aimed to functionalize different polymer surfaces with antimicrobial core/shell microcapsules. Microcapsules were made of sodium alginate in shell and filled with antimicrobial silver in their core prior to application on the surface of polymer materials by dip-coating methodology. Characterization of polymers after functionalization was performed by several spectroscopic and microscopic techniques. After the characterization of polymers before and after the functionalization, the release of the active substances was monitored in time. The obtained test results can help with the calculation on the minimal concentration of antimicrobial silver that is encapsulated to achieve the desired amounts of release over time.

Silver (Ag) and zinc (Zn) are very powerful antimicrobial metals. Therefore, in this research, a high-throughput, sensitive, and rapid method was developed for the determination of Ag and Zn in microcapsules using inductively coupled plasma mass spectrometry (ICP-MS). The sample preparation procedure employed simple microwave digestion of the microcapsules with 55.55% v/v HNO3 and 44.45% v/v H2O2. The method was applied to determine Ag and Zn in microcapsule samples of different sizes (120 and 450 μm) after their preparation with and without chitosan. Prepared microcapsules, after characterization, were bonded to a polymer carrier by sol-gel procedure and the materials were characterized by FTIR spectroscopy and high-resolution optical microscopy. Significant differences were found in Ag and Zn levels between microcapsules samples prepared with and without chitosan. The results have shown that samples with chitosan had up to 20% higher levels of Zn than Ag: 120 μm microcapsules contained 351.50 μg/g of Ag and 85.51 μg/g of Zn, respectively. In contrast, samples prepared without chitosan showed larger overall variability: In microcapsules with a diameter of 120 μm, the amounts of antimicrobial metals were 98.32 μg/g of Ag and 106.75 μg of Zn, respectively. Moreover, 450 μm microcapsules contained 190.98 μg/g of Ag and 121.35 μg/g of Zn. Those quantities are high enough for efficient antimicrobial activity of newly prepared microcapsules, enabling the application of microcapsules in different antimicrobial coatings.