Dehydration technique with 80% sulfuric acid was used to create a novel biochar from mandarin peel wastes followed by condensate with triethylenetetramine (TETA) to give Mandarin Biochar-TETA (MBT). BJH, BET, FTIR, SEM, DSC, TGA, and EDX studies were used to characterise the MBT. The capacity of the newly developed biochar to remove Acid Yellow 11 (AY11) dye from a water solution was studied. The pH of AY11 dye adsorption was found to be best at pH 1.5. Using 100 ppm AY11 dye as a beginning concentration and 1.75 g L–1 MBT dose, the greatest percent of AY11 dye removal by MBT was 97.83%. The MBT calculated maximum adsorption capacity (Qm) was 384.62 mg g–1. Langmuir (LIM), Freundlich (FIM), Tempkin (TIM), and Dubinin–Radushkevich (DRIM) isotherm models were applied to analyse the experimental data. Furthermore, the results of these isotherm models were investigated by various known error function equations. The MBT experimental data was best suited by the LIM. Pseudo-first-order (PFO), pseudo-second-order (PSO), Elovich kinetic model (EKM), intraparticle diffusion (IPD), and film diffusion (FD) models were used to calculate kinetic data. A PSO rate model with a high correlation (R2 > 0.990) was used to assess the adsorption rate. The main mechanism of the MBT adsorption method of the AY11 dye’s anions adsorption is the electrostatic attractive forces that arise with the increase of positively charged sites in an acidic medium. The obtained data suggest that the prepared MBT adsorbent has the potential to be an effective material to remove the AY11 dye from water and that it may be used repeatedly without losing its adsorption efficiency.

No abstract

This work demonstrates the preparation of high-surface-area activated carbon (AC) from Pisum sativum pods using ZnCl2 and KOH as activating agents. The influence of CO2 and N2 gases during the carbonization process on the porosity of AC were studied. The highest specific surface area of AC was estimated at 1300 to 1500 m2/g, which presented characteristics of microporous materials. SEM micrographs revealed that chemical activation using an impregnation reagent ZnCl2 increases the porosity of the AC, which in turn leads to an increase in the surface area, and the SEM image showed that particle size diameter ranged between 48.88 and 69.95 nm. The performance of prepared AC for adsorption of Acid Orange 7 (AO7) dye was tested. The results showed that the adsorption percentage by AC (2.5 g/L) was equal to 94.76% after just 15 min, and the percentage of removal increased to be ~100% after 60 min. The maximum adsorption capacity was 473.93 mg g−1. A Langmuir model (LM) shows the best-fitted equilibrium isotherm, and the kinetic data fitted better to the pseudo-second-order and Film diffusion models. The removal of AO7 dye using AC from Pisum sativum pods was optimized using a response factor model (RSM), and the results were reported.