The elastic response of (Ba,Ca)(Ti,Zr)O3 at compositions where the piezoelectric effect is maximized has been measured by different methods between 1 Hz and 250 kHz and compared with that of PZT at the middle of its morphotropic phase boundary. In all cases, the compliance is peaked at the border between the tetragonal (T) and the orthorhombic (O) phases, intermediate between the T and the low-temperature rhombohedral phase. The anomalies do not exhibit dependence on frequency and their relative amplitude is 200–300 times larger than the losses, demonstrating that they are intrinsic rather than due to the domain wall motion. This also demonstrates the role of an intermediate O or monoclinic phase in enhancing the transverse instability and piezoelectric coupling at a (morphotropic) phase boundary between R and T phases.

Epitaxial (1 - x)Ba(Ti0.8Zr0.2)TiO3 - x(Ba0.7Ca0.3)TiO3, x = 0.45 (BCZT 45), thin films have been deposited on (001) SrTiO3 (STO) and (001/100) SrLaAlO4 (SLAO) substrates by pulsed laser deposition. X-ray diffraction and high-resolution transmission electron microscopy (HRTEM) confirmed the epitaxial growth of the films. A high structural quality has been evidenced for the BCZT/STO films. Geometric phase analysis (GPA) associated with the HRTEM enabled us to obtain microstrain analysis and the in-plane and out-of-plane lattice parameter variation on different areas. Tetragonality ratio fluctuations at nanoscale level which are relevant for the existence of nanodomains have been evidenced on the BCZT/STO films. The in-plane dielectric constant has been measured on interdigital electrodes deposited by lift-off technique on the top of the films. High values of dielectric permittivity (>3000) combined with low dielectric loss (<0.01) are obtained for BCZT 45 film deposited on STO substrate, showing nearly constant values between 1 kHz and 10 MHz. The high dielectric permittivity of BCZT thin films was attributed to their high structural quality and to the loss of rotation stability of the polarization associated with the presence of nanodomains. This results into a divergence of fluctuations of polarization direction and a peak of dielectric susceptibility. The enhanced switching of such nanodomain configuration was probed by piezoforce microscopy, by writing and reading domains during topography scanning.

No abstract

BiFeO3 is one of the most promising multiferroic materials but undergoes two major drawbacks: low dielectric susceptibility and high dielectric loss. Here we report high in-plane dielectric permittivity (ε’ ∼2500) and low dielectric loss (tan δ < 0.01) obtained on Bi0.95Y0.05FeO3 films epitaxially grown on SrTiO3 (001) by pulsed laser deposition. High resolution transmission electron microscopy and geometric phase analysis evidenced nanostripe domains with alternating compressive/tensile strain and slight lattice rotations. Nanoscale mixed phase/domain ensembles are commonly found in different complex materials with giant dielectric/electromechanical (ferroelectric/ relaxors) or magnetoresistance (manganites) response. Our work brings insight into the joined role of chemical pressure and epitaxial strain on the appearance of nanoscale stripe structure which creates conditions for easy reorientation and high dielectric response, and could be of more general relevance for the field of materials science where engineered materials with huge response to external stimuli are a highly priced target.

Developing a controlled method for obtaining hybrid enzymatic-based interfaces for sensing application require the use of a multiuse, reusable sensor. By controlling the interface characteristics in terms of the surface chemistry, thickness, and roughness, a tailored response toward various toxic compounds can be obtained, regarding both materials used as active surfaces and fabrication methods. Herein, we report a preliminary study on using a laser-based method (i.e., matrix-assisted pulsed laser evaporation, or MAPLE) for obtaining active polymeric–enzymatic interfaces as hybrid or layered coatings for detecting toxic vapors. The MAPLE fabrication consisted of the simultaneous alternating evaporation of layers of polyethylenimine (PEI) and acetylcholinesterase (AchE) in order to obtain active surfaces as both hybrid PEI-AchE and a PEI/AchE layered coating, respectively. The deposition processes of the polymer and enzyme were carried out using a double-target system and a Nd:YAG pulsed laser, operating at 0.45 J/cm2 fluences with a wavelength of 266 nm and a repetition rate of 10 Hz. Fourier transform infrared spectroscopy revealed no significant changes in the functional groups of both hybrid and layered coatings compared with the initial material. The thickness and roughness, as well as the morphologies of the coatings revealed by atomic force microscopy and scanning electron microscopy showed coatings thicker than two μm that had smooth surfaces and average roughness values below six nm. The sensors were tested with simulants for nerve gases and pesticides containing phosphonate ester groups, namely dimethyl methylphosphonate (DMMP) and diisopropyl methylphosphonate (DIMP), and a different sensitivity was shown to the selected chemical agents for each of the sensors. The best sensitivities for DMMP and DIMP obtained by using a PEI-AchE coated sensor are 65 kHz and 200 kHz, respectively, whereas the best sensitivity when using multilayered interfaces is 30 kHz and 10 KHz for DIMP and DMMP, respectively.