No abstract

We reported on three-dimensional (3D) superparamagnetic scaffolds that enhanced the mineralization of magnetic nanoparticle-free osteoblast cells. The scaffolds were fabricated with submicronic resolution by laser direct writing via two photons polymerization of Ormocore/magnetic nanoparticles (MNPs) composites and possessed complex and reproducible architectures. MNPs with a diameter of 4.9 ± 1.5 nm and saturation magnetization of 30 emu/g were added to Ormocore, in concentrations of 0, 2 and 4 mg/mL. The homogenous distribution and the concentration of the MNPs from the unpolymerized Ormocore/MNPs composite were preserved after the photopolymerization process. The MNPs in the scaffolds retained their superparamagnetic behavior. The specific magnetizations of the scaffolds with 2 and 4 mg/mL MNPs concentrations were of 14 emu/g and 17 emu/g, respectively. The MNPs reduced the shrinkage of the structures from 80.2 ± 5.3% for scaffolds without MNPs to 20.7 ± 4.7% for scaffolds with 4 mg/mL MNPs. Osteoblast cells seeded on scaffolds exposed to static magnetic field of 1.3 T deformed the regular architecture of the scaffolds and evoked faster mineralization in comparison to unstimulated samples. Scaffolds deformation and extracellular matrix mineralization under static magnetic field (SMF) exposure increased with increasing MNPs concentration. The results are discussed in the frame of gradient magnetic fields of ~3 × 10−4 T/m generated by MNPs over the cells bodies.

Epitaxial (1 - x)Ba(Ti0.8Zr0.2)TiO3 - x(Ba0.7Ca0.3)TiO3, x = 0.45 (BCZT 45), thin films have been deposited on (001) SrTiO3 (STO) and (001/100) SrLaAlO4 (SLAO) substrates by pulsed laser deposition. X-ray diffraction and high-resolution transmission electron microscopy (HRTEM) confirmed the epitaxial growth of the films. A high structural quality has been evidenced for the BCZT/STO films. Geometric phase analysis (GPA) associated with the HRTEM enabled us to obtain microstrain analysis and the in-plane and out-of-plane lattice parameter variation on different areas. Tetragonality ratio fluctuations at nanoscale level which are relevant for the existence of nanodomains have been evidenced on the BCZT/STO films. The in-plane dielectric constant has been measured on interdigital electrodes deposited by lift-off technique on the top of the films. High values of dielectric permittivity (>3000) combined with low dielectric loss (<0.01) are obtained for BCZT 45 film deposited on STO substrate, showing nearly constant values between 1 kHz and 10 MHz. The high dielectric permittivity of BCZT thin films was attributed to their high structural quality and to the loss of rotation stability of the polarization associated with the presence of nanodomains. This results into a divergence of fluctuations of polarization direction and a peak of dielectric susceptibility. The enhanced switching of such nanodomain configuration was probed by piezoforce microscopy, by writing and reading domains during topography scanning.

No abstract

No abstract