AZ91 Mg alloy was micro arc oxidized under constant electrical parameters in silicate based and phosphate based electrolytes with and without addition of organic chemicals, namely Hexamethylenetetramine (HMTA), TRIS (hydroxymethyl) aminomethane (THAM) and Glycerol in two different concentrations. Following oxidation, samples were characterized by X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), coating thickness measurements, hardness measurements and electrochemical corrosion tests. Results showed that coating layers mainly consisted of MgO, Mg2SiO4 and MgF2 for silicate based electrolytes, and MgO for phosphate based electrolytes. Incorporation of organic chemicals into electrolyte composition did not change the type of the phases in the coating. However, when they are added in silicate based electrolytes, pore density and coating thickness are reduced and pore size is increased. On the other hand, there is no significant change in surface morphology when organic chemicals are added in phosphate based electrolyte. In the view point of corrosion resistance, organic chemicals did not enhance corrosion resistance of the samples oxidized in silicate based electrolytes, but exhibited some increment in corrosion resistance of the samples oxidized in phosphate based electrolytes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.