Improving current injection into r- and m-planes of nanowires (NWs) is essential to realizing efficient GaInN/GaN multiple quantum shell (MQS) NW-based light-emitting diodes (LEDs). Here, we present the effects of different p-GaN shell growth conditions on the emission characteristics of MQS NW-LEDs. Firstly, a comparison between cathodoluminescence (CL) and electroluminescence (EL) spectra indicates that the emission in NW-LEDs originates from the top region of the NWs. By growing thick p-GaN shells, the variable emission peak at around 600 nm and degradation of the light output of the NW-LEDs are elaborated, which is attributable to the localization of current in the c-plane region with various In-rich clusters and deep-level defects. Utilizing a high growth rate of p-GaN shell, an increased r-plane and a reduced c-plane region promote the deposition of indium tin oxide layer over the entire NW. Therefore, the current is effectively injected into both the r- and m-planes of the NW structures. Consequently, the light output and EL peak intensity of the NW-LEDs are enhanced by factors of 4.3 and 13.8, respectively, under an injection current of 100 mA. Furthermore, scanning transmission electron microscope images demonstrate the suppression of dislocations, triangular defects, and stacking faults at the apex of the p-GaN shell with a high growth rate. Therefore, localization of current injection in nonradiative recombination centers near the c-plane was also inhibited. Our results emphasize the possibility of realizing high efficacy in NW-LEDs via optimal p-GaN shell growth conditions, which is quite promising for application in the long-wavelength region.
Multi-color emission was identified from coaxial GaInN/GaN multiple-quantum-shells (MQS) nanowire-based light-emitting diodes (LEDs). In this study, the MQS nanowire samples for LED processes were selectively grown on patterned commercial GaN/sapphire...
The morphology and crystalline quality of p-GaN shells on coaxial GaInN/GaN multiple quantum shell (MQS) nanowires (NWs) were investigated using metal–organic chemical vapor deposition. By varying the trimethylgallium (TMG) flow rate, Mg doping, and growth temperature, it was verified that the TMG supply and growth temperature were the dominant parameters in the control of the p-GaN shape on NWs. Specifically, a sufficiently high TMG supply enabled the formation of a pyramid-shaped NW structure with a uniform p-GaN shell. The ratio of the growth rate between the c- and m-planes on the NWs was calculated to be approximately 0.4545. High-angle annular dark-field scanning transmission electron microscopy characterization confirmed that no clear extended defects were present in the n-GaN core and MQS/p-GaN shells on the sidewall. Regarding the p-GaN shell above the c-plane MQS region, only a few screw dislocations and Frank-type partial dislocations appeared at the interface between the serpentine c-plane MQS and the p-GaN shell near the tips. This suggested that the crystalline quality of the MQS structure can trigger the formation of screw dislocations and Frank-type partial dislocations during the p-GaN growth. The growth mechanism of the p-GaN shell on NWs was also discussed. To inspect the electronic properties, a prototype of a micro light-emitting diode (LED) with a chip size of 50 × 50 μm2 was demonstrated in the NWs with optimal growth. By correlating the light output curve with the electroluminescence spectra, three different emission peaks (450, 470, and 510 nm) were assignable to the emission from the m-, r-, and c-planes, respectively.
GaInN/GaN multi-quantum-shell (MQS) nanowires (NWs) are gaining increasing attention as promising materials for developing highly efficient long-wavelength micro-light emitting diodes (LEDs). To improve the emission properties in GaInN/GaN MQS NWs, it is necessary to suppress the emission from the (0001) c-plane MQS at the apex region, which featured with low crystalline quality. In this study, we investigated the enhancement of optical properties and the realization of micro-LEDs by confirming the effect of the (0001) plane region. A 7.9-fold enhancement of the electroluminescence (EL) intensity was demonstrated by removal the (0001) plane region via inductively coupled plasma (ICP) dry etching, owing to the promoted current injection into the (1–101) semi-polar and (10–10) non-polar sidewall area. To investigate the effect of the emission area on the samples with and without truncated (0001) plane region, devices with three different mesa areas (50 × 50, 100 × 100, and 100 × 200 μm2) were fabricated. An increased EL intensity with the reduced mesa areas was observed in the samples without dry etching of the (0001)-plane area, because more current can be injected into the sidewall region with higher crystalline quality and luminous efficiency than the (0001)-plane MQS. Under the same injection current density, the truncated samples’ light output was increased for more than ten times as compared to the samples without (0001)-plane etching. Therefore, it confirms the possibility of realizing highly efficient GaInN/GaN MQS NWs LEDs by eliminating the (0001) plane MQS region. A precise etching and surface passivation of the apex region is expected to further reduce the reverse leakage current and improve the performance in NW-LEDs.
Core−shell GaInN/GaN multiquantum shell (MQS) nanowires (NWs) are gaining great attention for high-efficiency microlight-emitting diodes (micro-LEDs) owing to the minimized etching region on their sidewall, nonpolar or semipolar emission planes, and ultralow density of dislocations. In this study, we evaluated the changes in NW morphologies and the corresponding device properties induced by GaInN/GaN superlattice (SL) structures. The cathodoluminescence intensities of the samples with 20 and 40 pairs of SLs were about 2.2 and 3.4 times higher, respectively, than that of the sample without SLs. The high-resolution scanning transmission electron microscopy (STEM) inspection confirmed that the high growth temperature of SLs prevented growth in the semipolar plane region close to the n-GaN core. A similar phenomenon was also observed for the GaN quantum barriers of the semipolar MQS region under a high growth temperature of 810 °C. This phenomenon was ascribed to the passivation of the semipolar plane surface by hydrogen atoms and the high probability of decomposition through NH 3 or N−H-related bonds. Although no clear SL grew on the semipolar plane near the n-core region, the top area of the nonpolar plane SL was expected to adequately suppress the point defects propagating from the n-GaN core to the semipolar plane MQS. The electroluminescence (EL) spectra and light output curves demonstrated a clear enhancement of more than 3-folds compared to the fabricated micro-LEDs without SL structures, which was associated with the improved crystalline quality of the MQS and enlarged area of the semipolar planes. Moreover, by increasing the growth time of GaN quantum barriers, the EL emission intensity of the micro-LED devices exhibited a 4-fold improvement owing to the reduced carrier overflow in the thickened GaN barriers on the semipolar (11̅ 01) planes. Thus, the results verified the possibility of realizing highly efficient NW-based micro-LEDs by optimizing the NW morphology using SL structures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.