Self-biased magnetoelectric composites, which are realized with the exchange bias effect, hold an increased total anisotropy field compared to systems without exchange bias. Thus, small exchange bias fields are favorable because of a minor reduction of magnetic permeability and magneto-electric voltage coefficient. However, weakly biased magnetoelectric composites lose their self-biasing properties and possibly show an increase of discontinuities in magnetization reversal due to the formation of magnetic domains. By a thickness variation of the ferromagnetic layer, a maximum voltage coefficient αME ≈ 430 V/cm Oe was found for a magnetostrictive multilayer of 3 × (5 nm Ta/3 nm Cu/8 nm Mn-Ir/333 nm Fe-Co-Si-B). Yet, a stable single domain state indicating a well defined magnetization reversal by coherent magnetization rotation was achieved for layer thicknesses up to 100 nm Fe-Co-Si-B with αME ≈ 340 V/cm Oe. This slight reduction is overcompensated by the improved control of the magnetic domain pattern which is highly beneficial for magnetic field sensing applications and of special importance, when frequency conversion techniques are applied.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.