Poly(3-hydroxybutyrate) (PHB) and poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) are biopolyesters reported to provide favorable microenvironments for cell culture and possess potential for tissue engineering applications. Both biopolymers have been investigated for applications in a variety of medical scenarios, including nerve and bone repair. This study investigated the influence these biomaterials exerted on cell cycle progression of olfactory ensheathing cells (OECs) and mesenchymal stem cells (MSCs) commonly used in the engineering of nerve and bone tissues. Cell cycle regulation is important for cell survival; analysis revealed that the biomaterials induced significant cell cycle progression in both MSCs and OECs. Significantly higher percentages of cells were cycled at synthesis (S) phase of the cycle on PHBV films compared to PHB, with MSCs more susceptible than OECs. Furthermore, detection of early stages of apoptotic activation showed significant differences in the two cell populations exhibiting necrosis and apoptosis when cultivated on the biomaterials. OECs compromised on PHB (5.6%) and PHBV (2.5%) compared to MSCs with 12.6% on PHB and 17% on PHBV. Significant differences in crystallinity and surface rugosity were determined between films of the two biomaterials, 88% and 1.12 μm for PHB and 76% and 0.72 μm for PHBV. While changes in surface properties may have influenced cell adhesion, the work presented here suggests that application of these biomaterials in tissue engineering are specific to cell type and requires a detailed investigation at the cell-material interface.
Electrospinning can produce nanofibrous scaffolds that mimic the architecture of the extracellular matrix and support cell attachment for tissue engineering applications. In this study, fibrous membranes of polyhydroxybutyrate (PHB) with various loadings of poly(L-lactide-co-ε-caprolactone) (PLCL) were successfully prepared by electrospinning. In comparison to PLCL scaffolds, PLCL blends with PHB exhibited more irregular fibre diameter distributions and higher average fibre diameters but there were no significant differences in pore size. PLCL/PHB scaffolds were more hydrophilic (<120°) with significantly reduced tensile strength (ca. 1 MPa) compared to PLCL scaffolds (150.9 ± 2.8° and 5.8 ± 0.5 MPa). Increasing PLCL loading in PHB/PLCL scaffolds significantly increased the extension at break, (4–6-fold). PLCL/PHB scaffolds supported greater adhesion and proliferation of olfactory ensheathing cells (OECs) than those exhibiting asynchronous growth on culture plates. Mitochondrial activity of cells cultivated on the electrospun blended membranes was enhanced compared to those grown on PLCL and PHB scaffolds (212, 179, and 153%, resp.). Analysis showed that PLCL/PHB nanofibrous membranes promoted cell cycle progression and reduced the onset of necrosis. Thus, electrospun PLCL/PHB composites promoted adhesion and proliferation of OECs when compared to their individual PLCL and PHB components suggesting potential in the repair and engineering of nerve tissue.
The addition of poly(ethylene glycol), PEG, to bioprocessing systems producing polyhydroxyalkanoates (PHAs), has been reported as a means of their molecular weight control and can also support bioPEGylation, resulting in hybrids with amphiphillic properties. However, the study of such natural-synthetic hybrids of PHA-b-PEG is still in its infancy. In this study, we report the influence of bioPEGylation of polyhydroxyoctanoate (PHO) on its physiochemical, material, and biological properties. Consistent with previous studies, bioPEGylation with diethylene glycol (DEG) showed a significant reduction in PHA molecular weight (57%). In comparison to solvent cast films of PHO, PHO-b-DEG films possessed a noticeable X-ray diffraction peak at 9.82 degrees and increased Young's modulus of 11 Gpa (83%). Potential biocompatibility was investigated by measuring the early phase of apoptosis in myoblastic satellite-stem cells (C2C12). Comparative analysis of cell proliferation and progression in the presence of the mcl-PHA and its hybrid showed that the latter induced significant cell cycle progression: the first time a biomaterial has been shown to do so. Microtopographies of the film surfaces demonstrated that these differences were not due to changes in surface morphology; both polymers possessed average surface rugosities of 1.4 +/- 0.2 microm. However, a slight decrease in surface hydrophobicity (3.5 +/- 0.9 degrees) due to the hydrophilic DEG may have exerted an influence. The results support the further study of bioPEGylated PHAs as potential biomaterials in the field of tissue engineering.
Blending poly[(l‐lactide)‐co‐(ε‐caprolactone)] with 2.0% (w/w) collagen significantly changes electrospun fibre morphology, which assists in improving the initial attachment and health of olfactory ensheathing cells.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.