Ultra micro-indentation tests on Ni and Cu samples showed increasing hardness with decreasing penetration depth over a range from 200 to 2000 nm. The results suggest increased strain hardening with decreased indentation depth. To establish that this is a real material effect, a series of tests were conducted on amorphous materials, for which strain hardening is not expected. The hardness of Metglas® was found to be independent of depth. A simple model of the dislocation densities produced under the indenter tip describes the data well. The model is based on the fact that the high density of dislocations expected under a shallow indentation would cause an increase in measured hardness. At large depths, the density of geometrically necessary dislocations is sufficiently small to have little effect on hardness, and the measured hardness approaches the intrinsic hardness of the material.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.