While the discovery of two-dimensional (2D) magnets opens the door for fundamental physics and next-generation spintronics, it is technically challenging to achieve the room-temperature ferromagnetic (FM) order in a way compatible with potential device applications. Here, we report the growth and properties of single- and few-layer CrTe2, a van der Waals (vdW) material, on bilayer graphene by molecular beam epitaxy (MBE). Intrinsic ferromagnetism with a Curie temperature (TC) up to 300 K, an atomic magnetic moment of ~0.21 $${\mu }_{{\rm{B}}}$$ μ B /Cr and perpendicular magnetic anisotropy (PMA) constant (Ku) of 4.89 × 105 erg/cm3 at room temperature in these few-monolayer films have been unambiguously evidenced by superconducting quantum interference device and X-ray magnetic circular dichroism. This intrinsic ferromagnetism has also been identified by the splitting of majority and minority band dispersions with ~0.2 eV at Г point using angle-resolved photoemission spectroscopy. The FM order is preserved with the film thickness down to a monolayer (TC ~ 200 K), benefiting from the strong PMA and weak interlayer coupling. The successful MBE growth of 2D FM CrTe2 films with room-temperature ferromagnetism opens a new avenue for developing large-scale 2D magnet-based spintronics devices.

No abstract

No abstract

No abstract

ZnO films were synthesized on GaAs substrates at different growth conditions by pulse laser deposition. High-purity ͑99.999%͒ oxygen was used as the ambient gas. The pressure of the ambient oxygen gas for ZnO film growth was varied from 20 to 50 mTorr, and the growth temperature from 300 to 450°C. ZnO films showed very strong bound exciton peaks located between 3.37 and 3.35 eV. The full width at half maximum of the bound exciton peak is less than 5 meV. These results indicate ZnO films on GaAs substrates can be used for optical devices such as light-emitting diodes. The other significant properties of textured ZnO films on GaAs substrates are described.