Lithium iron arsenide phases with compositions close to LiFeAs exhibit superconductivity at temperatures at least as high as 16 K, demonstrating that superconducting [FeAs](-) anionic layers with the anti-PbO structure type occur in at least three different structure types and with a wide range of As-Fe-As bond angles.

Lithium dendrite (filament) propagation through ceramic electrolytes, leading to short-circuits at high rates of charge, is one of the greatest barriers to realising high energy density all-solidstate lithium anode batteries. Utilising in-situ X-ray computed tomography coupled with spatially mapped X-ray diffraction, the propagation of cracks and the propagation of lithium dendrites through the solid electrolyte have been tracked in a Li/Li6PS5Cl/Li cell as a function of the charge passed. On plating, cracking initiates with spallation, conical "pothole"-like cracks that form in the ceramic electrolyte near the surface with the plated electrode. The spallations form predominantly at the lithium electrode edges where local fields are high. Transverse cracks then propagate from the spallations across the electrolyte from the plated to the stripped electrode. Lithium ingress drives the propagation of the spallation and transverse cracks by widening the crack from the rear, i.e. the crack front propagates ahead of the Li. As a result, cracks traverse the entire electrolyte before the Li arrives at the other electrode and therefore before a short-circuit occurs.

A series of layered oxychalcogenide and oxypnictide solids is described that contain oxide layers separated by distinct layers, which contain the softer chalcogenide (S, Se, Te) or pnictide (P, As, Sb, Bi) anions. The relationships between the crystal structures adopted by these compounds are described, and the physical and chemical properties of these materials are related to the structures and the properties of the elements. The properties exhibited by the oxychalcogenide materials include semiconductor properties, for example, in LaOCuCh (Ch = chalcogenide) and derivatives, unusual magnetic properties exhibited by the class Sr 2MO 2Cu 2-deltaS 2 (M = Mn, Co, Ni), and redox properties exhibited by the materials Sr 2MnO 2Cu 2 m-0.5 S m+1 ( m = 1-3) and Sr 4Mn 3O 7.5Cu 2Ch 2 (Ch = S, Se). Recent results in the oxychalcogenide area are reviewed, and some new results on the intriguing series of compounds Sr 2MO 2Cu 2-deltaS 2 (M = Mn, Co, Ni) are reported. Oxypnictides have received less recent attention, but this is changing: a new frenzy of research is underway following the discovery of high-temperature superconductivity (>40 K) in derivatives of the layered oxyarsenide LaOFeAs. The early results in this exciting new area will be reviewed.

Three-electrode studies coupled with tomographic imaging of the Na/Na-β″-alumina interface reveal that voids form in the Na metal at the interface on stripping and they accumulate on cycling, leading to increasing interfacial current density, dendrite formation on plating, short circuit, and cell failure. The process occurs above a critical current for stripping (CCS) for a given stack pressure, which sets the upper limit on current density that avoids cell failure, in line with results for the Li/solid-electrolyte interface. The pressure required to avoid cell failure varies linearly with current density, indicating that Na creep rather than diffusion per se dominates Na transport to the interface and that significant pressures are required to prevent cell death, >9 MPa at 2.5 mA·cm–2.