Commercial polyolefin separators exhibit problems including shrinkage under high temperatures and poor electrolyte wettability and uptake, resulting in low ionic conductivity and safety problems. In this work, core–shell silica-polyphosphazene nanoparticles (SiO2@PZS) with different PZS layer thicknesses were synthesized and coated onto both sides of polyethylene (PE) microporous membranes to prepare composite membranes. Compared to pure silica-coated membranes and PE membranes, the PE-SiO2@PZS composite membrane had higher ionic conductivity. With the increase in the SiO2@PZS shell thickness, the electrolyte uptake, ionic conductivity and discharge capacity gradually increased. The discharge capacity of the PE-SiO2@PZS composite membrane at 8 C rate was 129 mAh/g, which was higher than the values of 107 mAh/g for the PE-SiO2 composite membrane and 104 mAh/g for the PE membrane.
Polymer matrix nanomaterials have revolutionized materials science due to their unique properties resulting from the incorporation of nanoscale fillers into polymer matrices [...]
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.