To improve the wear resistance of high-strength and high-conductivity Cu–Cr–Zr alloys in high-speed and heavy load friction environments, coatings including Ni–Cu, Ni–Cu-10(W,Si), Ni–Cu–10(Mo,W,Si), and Ni–Cu–15(Mo,W,Si) (with an atomic ratio of Mo,W to Si of 1:2) were prepared using coaxial powder-feeding laser cladding technology. The microstructure and wear performance of coatings were chiefly investigated. The results revealed that (Mo,W)Si2 and MoNiSi phases are found in the Ni–Cu–10(Mo,W,Si) and Ni–Cu–15(Mo,W,Si) coating. WSi2 phases are found in the Ni–Cu–10(W,Si) coating. The degree of grain refinement in Ni–Cu–10(Mo,W,Si) was greater than that of the Ni–Cu–10(W,Si) coating after the effect of Mo. The excellent wear resistance and micro-hardness of the Ni–Cu–15(Mo,W,Si) coating were attributed to the increase in its dispersion phase, which were approximately 34.72 mg/km and 428 HV, 27.1% and 590% higher than the Cu–Cr–Zr substrate, respectively. The existence of silicide plays an important role in grain refinement due to the promotion of nucleation and the inhibition of grain growth. In addition, the wear mechanism transformed from adhesive wear in the Ni–Cu coating with no silicides to abrasive wear in the Ni–Cu–15(Mo,W,Si) coating with high levels of silicides.
A cold spray–laser cladding composite gradient coating (CLGC) was successfully formed on a Cu substrate. In comparison with traditional laser cladding gradient coatings (LGC), cold spraying the pre-set Ni-Cu alloy’s intermediate transition layer not only mitigates the negative impacts due to the high reflectivity of the copper substrate but also helps to minimize the difference in the coefficients of thermal expansion (CTE) between the substrate and coating. This reduces the overall crack sensitivity and improves the cladding quality of the coating. Besides this, the uniform distribution of hard phases in CLGC, such as Ni11Si12 and Mo5Si3, greatly increases its microhardness compared to the Cu substrate, thus resulting in the value of 478.8 HV0.5 being approximately 8 times that of the Cu substrate. The friction coefficient of CLGC is lowered compared to both the Cu substrate and LGC with respective values of 0.28, 0.54, and 0.43, and its wear rate is only one-third of the Cu substrate’s. These results suggest CLGC has excellent anti-wear properties. In addition, the wear mechanism was determined from the microscopic morphology and element distribution and was found to be oxidative and abrasive. This approach combines cold spraying and laser cladding to form a nickel-based gradient coating on a Cu substrate without cracks, holes, or other faults, thus improving the wear resistance of the Cu substrate and improving its usability.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.