Three different biological systems, the consortium of autotrophic bacteria Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans, heterotrophic fungus Aspergillus niger and heterotrophic yeast Rhodotorula mucilaginosa, were investigated for lithium extraction from lepidolite. The bacterial consortium was the most effective, 11 mg l −1 of Li was dissolved in the absence of nutrients within 336 days. Fungal and yeast bioleaching was faster (40 days), however, with lower extraction efficiency. Bioaccumulation represented a main process of Li extraction by R. mucilaginosa and A. niger, with 92 and 77% of total extracted Li accumulated in the biomass, respectively. The X-ray diffraction analysis for bioleaching residue indicated changes caused by microorganisms, however, with differences between bacterial leaching and bioleaching by fungi or yeasts. The final bioleaching yields for bacterial consortium, A. niger and R. mucilaginosa were 8.8%, 0.2% and 1.1%, respectively. two-step bioleaching using heterotrophic organisms followed by autotrophic bioleaching could lead to the increase of the process kinetics and efficiency. Bioaccumulation of Li offers strong advantage in Li extraction from solution.

The objective of this work was to evaluate the influence of static, stirring and shaking conditions on copper, zinc, nickel and aluminium dissolution from printed circuit boards (PCBs) using the mixed acidophilic bacterial culture of Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans. The results revealed that static conditions were the most effective in zinc and aluminium dissolution. Zinc was removed almost completely under static conditions, whereas maximum of nickel dissolution was reached under the stirring conditions. The highest copper recovery (36%) was reached under stirring conditions. The shaking conditions appeared to be the least suitable. The relative importance of these systems for the bioleaching of copper and nickel decreased in the order: stirring, static conditions, shaking.

The role of iron in metal-bearing waste bioleaching was studied. Four various types of waste (printed circuit boards (PCBs), Ni-Cd batteries, alkaline batteries and Li-ion batteries) were treated by bioleaching using the acidophilic bacteria A. ferrooxidans and A. thiooxidans (separately or in mixture). Role of main leaching agents (Fe 3+ ions or sulphuric acid) was simulated in abiotic experiments. Results showed that oxidation abilities of Fe 3+ ions were crucial for recovery of Cu and Zn from PCBs, with the efficiencies of 88% and 100%, respectively. To recover 68% of Ni from PCBs, and 55% and 100% of Ni and Cd, respectively, from Ni-Cd batteries both oxidation action and hydrolysis of Fe 3+ were required. The importance of Fe 2+ ions as a reducing agent was showed in bioleaching of Co from Li-ion batteries and Mn from alkaline batteries. The efficiency of the processes has increased by 70% and 40% in Co and Mn bioleaching, respectively, in the presence of Fe 2+ ions. Based on the results we suggest the integrated biometallurgical model of metal-bearing waste recycling in the effort to develop zero-waste and less energy-dependent technologies.