Oxygen reduction reaction (ORR) is increasingly being studied in oxide systems due to advantages ranging from cost effectiveness to desirable kinetics. Oxygen-deficient oxides like brownmillerites are known to enhance ORR activity by providing oxygen adsorption sites. In parallel, nitrogen and iron doping in carbon materials, and consequent presence of catalytically active complex species like C-Fe-N, is also suggested to be good strategies for designing ORR-active catalysts. A combination of these features in N-doped Fe containing brownmillerite can be envisaged to present synergistic effects to improve the activity. This is conceptualized in this report through enhanced activity of N-doped CaFeO brownmillerite when compared to its oxide parents. N doping is demonstrated by neutron diffraction, UV-vis spectroscopy, X-ray photoelectron spectroscopy, and X-ray absorption spectroscopy. Electrical conductivity is also found to be enhanced by N doping, which influences the activity. Electrochemical characterization by cyclic voltammetry, rotating disc electrode, and rotating ring disk electrode (RRDE) indicates an improved oxygen reduction activity in N-doped brownmillerite, with a 10 mV positive shift in the onset potential. RRDE measurements show that the compound exhibits 4-electron reduction pathways with lower HO production in the N-doped system; also, the N-doped sample exhibited better stability. The observations will enable better design of ORR catalysts that are stable and cost-effective.
Herein, we report the synthesis of a nitrogen-doped graphene (NGr) interpenetrated 3D Ni-nanocage (Ni-NGr) electrocatalyst by a simple water-in-oil (w/o) emulsion technique for oxidation of water to dioxygen. Correlation of adsorption of NGr and subsequent interpenetration through the specific surface plane of nickel particles as well as the concomitant interaction of N and C with Ni in the nano-regime has been investigated. Apart from the benefits of the synergistic interactions between Ni, N, and C, the overall integrity of the structure and its intra-molecular connectivity within the framework help in achieving better oxygen evolution characteristics at a significantly reduced overpotential. The engineered Ni-NGr nanocage displays a substantially low overpotential of ∼290 mV at a practical current density of 20 mA cm(-2) in 0.1 M KOH. In comparison, NGr and Ni-particles as separate entities give overpotentials of ∼570 and ∼370 mV under similar conditions. Moreover, the long term stability of Ni-NGr was investigated by anodic potential cycling for 500 cycles and an 8.5% increment in the overpotential at 20 mA cm(-2) was observed. Additionally, a chronoamperometric test was performed for 15 h at 20 mA cm(-2), which highlights the better sustainability of Ni-NGr under the actual operating conditions. Finally, the quantitative estimation of evolved oxygen was monitored by gas chromatography and was found to be 70 mmol h(-1) g(-1) of oxygen, which is constant in the second cycle as well.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.