This study shows mechanochemical synthesis as an alternative method to the traditional green synthesis of silver nanoparticles in a comparative manner by comparing the products obtained using both methodologies and different characterization methods. As a silver precursor, the most commonly used silver nitrate was applied and the easily accessible lavender (Lavandula angustofolia L.) plant was used as a reducing agent. Both syntheses were performed using 7 different lavender:AgNO3 mass ratios. The synthesis time was limited to 8 and 15 min in the case of green and mechanochemical synthesis, respectively, although a significant amount of unreacted silver nitrate was detected in both crude reaction mixtures at low lavender:AgNO3 ratios. This finding is of particular interest mainly for green synthesis, as the potential presence of silver nitrate in the produced nanosuspension is often overlooked. Unreacted AgNO3 has been removed from the mechanochemically synthesized samples by washing. The nanocrystalline character of the products has been confirmed by both X-ray diffraction (Rietveld refinement) and transmission electron microscopy. The latter has shown bimodal size distribution with larger particles in tens of nanometers and the smaller ones below 10 nm in size. In the case of green synthesis, the used lavender:AgNO3 ratio was found to have a decisive role on the crystallite size. Silver chloride has been detected as a side-product, mainly at high lavender:AgNO3 ratios. Both products have shown a strong antibacterial activity, being higher in the case of green synthesis, but this can be ascribed to the presence of unreacted AgNO3. Thus, one-step mechanochemical synthesis (without the need to prepare extract and performing the synthesis as separate steps) can be applied as a sustainable alternative to the traditional green synthesis of Ag nanoparticles using plants.

Coating of the biodegradable metals represents an effective way of modification of their properties. Insufficient biological, mechanical, or degradation performance of pure metals may be enhanced when the proper type of organic polymer coating is used. In our previous work, the significant effect of the polyethyleneimine (PEI) coating not only on the rate but also on the type of corrosion was discovered. To bring a comprehensive overview of the Fe-PEI system performance, iron-based biodegradable scaffolds with polyethyleneimine coating were studied and their cytocompatibility and hemocompatibility, and mechanical properties were evaluated and discussed in this work. Electrochemical impedance spectroscopy (EIS) measurements were conducted for further study of material behavior. Biological analyses (MTS assay, fluorescent imaging, hemocompatibility tests) showed better cell proliferation on the surface of Fe-PEI samples but not sufficient overall cytocompatibility. Good anti-platelet adhesion properties but higher hemolysis when compared to the pure iron was also observed for the coated samples. Mechanical properties of the prepared Fe-PEI material were enhanced after coating. These findings suggest that the Fe-PEI may be an interesting potential biomaterial after further composition optimization resulting in lower cytotoxicity and better hemocompatibility.