Present research concentrates on the process of anthraquinone degradation in the course of hydrogenation carried out in the presence of palladium catalyst. Hydrogenation experiments were carried out using agitated glass laboratory batch type reactor at atmospheric pressure of hydrogen and temperature of 55°C. Catalytic tests were performed using solutions composed of 2-ethyl-9,10-anthraquinone (eAQ) and a mixture of eAQ and 2-ethyloxanthrone (OXO) with various proportions. Degradation of anthraquinone was studied and in particular, the role of reduced forms of quinone namely hydroquinone and its tautomer OXO is discussed. A difference in the course of reactions pathways: hydrogenation of aromatic rings to give 2-ethyl-5,6,7,8-tetrahydro-9,10-anthraquinone (active quinone) and hydrogenolysis reactions yielding degradation products was observed.
Poly(methylvinylsiloxane) (V 3 polymer) obtained by kinetically controlled anionic ring-opening polymerization of 1,3,5-trimethyl-1,3,5-trivinylcyclotrisiloxane was cross-linked with various amounts of 1,3,5,7-tetramethylcyclotetrasiloxane (D 4 H ) in w/o high internal phase emulsions (HIPEs). PolyHIPEs thus prepared differed in the polymer cross-linking degree, which affected their porous morphology and total porosity. The obtained V 3 polymer-based polyHIPEs were applied as matrices for the incorporation of Pd from the Pd(OAc) 2 solution in tetrahydrofuran. This process involved the conversion of Si−H groups remaining in the polymer networks and resulted in the formation of crystalline, metallic Pd in the systems. Mean sizes of the generated Pd crystallites were lower in polyHIPEs of higher than in those of lower polymer cross-linking degrees and porosities (∼5 nm vs ∼8 nm, respectively). The Pd-containing polyHIPEs showed activity in catalytic hydrogenation of the triple carbon−carbon bond in phenylacetylene giving the unsaturated product, styrene with a selectivity of ca. 80%. To the best of our knowledge, this is the first work devoted to polysiloxane-based polyHIPEs with dispersed metallic particles.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.