This study evaluated protocols to eliminate acetone from dental adhesives and their effect on the kinetic of water sorption and percent of conversion of these adhesives. Experimental methacrylate-based adhesives with increasing hydrophilicity (R2, R3, R5) were used as reference materials. Primer-like solutions were prepared by addition of 50 wt% acetone. Acetone elimination was measured gravimetrically before and after: a spontaneous evaporation, an application of air-drying at room temperature or application of 40°C air-drying. Protocols were performed from 15 to 60 s. Specimens of adhesive/acetone mixtures were photo-activated and tested for degree of conversion, water sorption and solubility. Data were analyzed by ANOVA and Bonferroni's tests (α = 0.05). Complete acetone elimination was never achieved, but it was significantly greater after the 40°C air-drying application. Higher acetone elimination was observed for the least hydrophilic adhesive. Longer periods for acetone evaporation and heated air-stream can optimize polymerization and reduce the water sorption/solubility of adhesive system models.

Clinical RelevanceDespite oxalate desensitizer showing a decrease in the rate of resin-dentin bond degradation over time, it compromised the baseline bond strength of etch-and-rinse adhesives to dentin. Further investigation regarding reliability of the combination of oxalate desensitizers and etch-and-rinse adhesives is required prior to implementation of this approach in the clinical routine. SUMMARYPotassium oxalate desensitizers were previously shown to effectively reduce the immediate permeability of resin-bonded dentin. The current study evaluated whether the effect of the combined application of oxalate with etch-and-rinse adhesives interferes with the durability of resindentin bonds when using etch-and-rinse adhesives. The bond strength of resin-bonded dentin specimens composed of two-step or three-step etch-and-rinse adhesives (Single Bond, One-Step and Scotchbond Multi-Purpose, respectively) BISCO, Inc). The treatment of dentin with potassium oxalate was shown to negatively affect the baseline bond strength of resin-bonded dentin specimens, regardless of the adhesive used (p<0.05). After storage, the bond strength of the resin-bonded interfaces was significantly reduced for all the tested groups (p<0.001). Nevertheless, the rate of decreasing bond strength was significantly lower for oxalatetreated specimens than for the controls (p<0.05).

No abstract