No abstract

Synthesis and high-temperature transformations of crosslinked polymers of the methacrylic ester of 4-vinyl-4'-(l-hydroxyethyl)diphenyloxide 13. A. ZAITSEV, C. I. KHRAMOVA, T. S. TSYGANKOVA, I. 0. GUSAROVA and S. V. LUKASOVAcademjof Sciences of USSR, Institute of Macromolecular Compounds, 199 004 Leningrad, USSH I R spectroscopy and differential scanning calorimetry were used to establish that by prolonged heating of mcthacrylic ester of 4-vinyl-4'-(1-hydroxyethyl)diphenyloxide a t 140 to 170 O C a highly crosslinked polymer is formed. Its transverse ester bridges are broken a t 170 to 190°C with the formation of methacrylic acid units and vinyl side groups. I t is shown that thermal treatment of t h e polymcr a t 190 t o 250°C results in polycyclization of neighbouring groups and post-crosslinking of polymer chains. Synthese und Hochtenzperaturverhalten von vernetzten Polymeren des Methacrylsaureesters von 4-Vinyl-$'-(l-hydroxyethyl)d iphenylozidMit tels IR-Spektroskopie und Differential-Scanning-Calorimetrie wurde festgestellt, daB bei langerem Erhitzen des Methacrylsaureesters von 4-Vinyl-4'-(1-hydroxyethyl)diphenyloxid bei 140 bis 4 70 "C ein hochvernetztes Polymer gebildet wird, dessen Vernetzungsesterbrucken bei 170 bis 190°C unter Bildung von Methacrylsaureeinheiten und Vinylseitengruppen aufgebrochen werden. Bei thermischer Behandlung des Polymcrs im Bereich 190 bis 25OoC erfolgt. I'olycyclisierung benachbarter Gruppen und Nachvernetzung der Polymerketten. Culcmea u ewco~omewnepamyplcsze n p e e p a q e m z mpexaeplcscx nomutepoe aemaEpuaoeozo 3$upa 4-eu~un-4'-(1oh-cu3muw)au$enu~o~cuaaMeTOAaMH I'fK-CIIeKTpOCKOnHII H Am@@epeHUHaJIbHOt CKaHHpylOIQet KaJIOpAMeTpHM yCTaHOBJIeH0, 'IT0 npll AJIATeJIb-HOM HarpeBaHHH MCTaKPHJIOBOrO 3@Hpa 4-BHHHJI-4'-( l-OKCH3THJI)AH@eHHJIOKCmAa npH140-170 "C 06pa3ye~CR rJ'CT0-CeTVaTbIt COIIOJIHMep, IIOnepeVHbIe CJIOHHO3@HpHbIe MOCTHKH KOTOpOrO pacqennfmTCR npH 170-190°C C 06paao-BaHHeM 3BeHbeB MeTaKpHJIOBOt KACJIOTbI A 60KOBhlX BHHHJIbHbIX rpynn. nOKa3aH0, 9TO npH TepMOO6pa6OTKe CO-IIOJlHMepa npH 190-250°C IIPOIICXOAAT nOJIHqHKJIH3aqHH COCeAHHX rpynn H IIOBTOpHOe CUlHBaHHe nOJIHMepHbIX qenet.

No abstract

No abstract

Bis-(Cvinylphenyl) ether (BVPhE) was obtained by the polycondensation of bis-[4-(l-hydroxyethyl)phenyl] ether and subsequent dehydration of the resulting polyether. T.he kinetics of three-dimensional polymerization of BVPhE in an inert medium and in the presence of air have been investigated by I R spectroscopy and differential scanning calorimetry. It is shown that poly-BVPhE is a highly crosslinked glassy polymer exhibiting high thermal stability and having a softening point of m 460OC. Synthese, Struktur und Eigenschuften von Poly [bis-(4-vinylphenyl) -ether]ether und nachfolgende Dehydrierung des erhaltenen Polyethers hergestellt. Die Kinetik der dreidimensionalen Polymerisation von BVPhE wurde in einem inerten Medium sowie in Luft mittels IR-Spektroskopie und DSC untersucht. Es wird gezeigt, da8 Poly-RVPhE ein hochvernetztes glasiges Polymer mit hoher thermischer Stabilitat und einem Erweichungspunkt von etwa 46OoC ist. Cunmea, c m p p m y p a u ceoiicmsa nonu o'uc(4-su~u~cg6en~oeoso) a&pa a@npa n nocnegymqe8 RernzpaTaqmi 06pa3ymqeroc~ npn BTOM npocToro n o n~a @~p a . MeTOAaMEi EIK-cnempocKo-E;HC(4-BHHHJI@eHIIJIOBhI8) 3@Hp (BBQ3) nOJIyWH IIOCpeRCTBOM IfOJIHKOHAeHCa~MIl 6nC[4-( 1-OKCE13TEIJI)@?HIIJIOBOI'O] nHII II AH@@epeHI(HaJIbHOfi CKaHHpyH)uea KaJIOPHMeTPHH HCCaeAOBaHa KUHeTEIKa TpeXMepHOa nOJIIIMepH3aqHki BBQ3 B ElHePTHOfi CpeAe II B IIPIICYTCTBHII BO3AyXa. nOKaSaH0, YTO n o n~f -~B @ 3IIpeRCTaBJIfIeT c0608 ryCT0CeT-llaThIfi CTeKJIOO6pa3HbI8 nOJIHMeP, IIMeIoJJ.@ BbICOKYH) TePMOCTO8KOCTb EI TeMIlepaTypy pa3MfIrYCHIIFi N 460°C.