Aim:This experimental study was designed to focus on the effects of bleaching on toothbrush abrasion in three types of composites with different filler size.Materials and Methods:Forty eight disks were prepared from three types of composite and divided into 6 groups. In the first three groups the abrasion test was done. The remaining groups were bleached and the abrasion test was performed. The weight of the samples before and after abrasion was measured. Statistical analysis was done with one-way ANOVA and Duncan test.Results:There was a significant difference in abrasion of composites with different filler size (P < 0.05). The most amount of abrasion was observed in Z100 after being bleached. An increase in abrasion was noticed in all three types of tested composite after bleaching.Conclusion:According to the findings, it is suggested to use a nano filled resin composite for restoration if the bleaching treatment is required.

Objectives:To evaluate the effect of amalgam corrosion products in non-discolored dentin on the bond strength of replaced composite resin.Materials and Methods:One hundred and sixty-one Class I cavities were prepared on extracted premolars and divided into seven groups. Group 1: Light-cured composite; Groups 2, 3, and 4: Amalgam stored in 37°C normal saline for respectively 1, 3, and 6 months and then replaced with composite leaving the cavity walls intact. Groups 5, 6, and 7: Identical to Groups 2, 3, and 4, except the cavity walls were extended 0.5 mm after amalgam removal. Eighteen specimens from each group were selected for shear bond strength testing, while on remaining five samples, elemental microanalysis was conducted. Data were analyzed using Mann-Whitney and Freidman (α = 0.05).Results:There was a significant difference between Groups 1 and 4 and also between Group 1 and Groups 5, 6, and 7. However, Groups 1, 2, and 3 showed no significant difference regarding bond strength. Bond strengths of Group 4 was significantly less than Groups 2 and 3. However, Groups 5, 6, and 7 showed similar bond strength. There was no difference among all groups in terms of metal elements at any storage times.