In this paper, the use of the Selective Laser Sintering (SLS) process for the generation of bone tissue engineering scaffolds from PCL and PCL/TCP is explored. Different scaffold designs are generated and are assessed from the point of view of manufacturability, porosity and mechanical performance. Large scaffold specimens are generated, with a preferred design, and are assessed through an in vivo study in a critical size bone defect in the sheep tibia with subsequent microscopic, histological and mechanical evaluation. Further explorations are performed to generate scaffolds with increasing TCP contents.Scaffold fabrication from PCL and PCL/TCP mixtures with up to 50 mass-% TCP is shown to be possible. With increasing macroporosity the stiffness of the scaffolds is seen to drop, however, the stiffness can be increased by minor geometrical changes, such as the addition of a cage around the scaffold. In the animal study the selected scaffold for implantation did not perform as well as the TCP control in terms of new bone formation and the resulting mechanical performance of the defect area. A possible cause for this is presented.

A current challenge in bone tissue engineering is to create scaffolds with suitable mechanical properties, high porosity, full interconnectivity and suitable pore size. In this paper, polyamide and polycaprolactone scaffolds were fabricated using a solid free form technique known as selective laser sintering. These scaffolds had fully interconnected pores, minimized strut thickness, and a porosity of approximately 55%. Tensile and compression tests as well as finite element analysis were carried out on these scaffolds. It was found that the values predicted for the effective modulus by the FE model were much higher than the actual values obtained from experimental results. One possible explanation for this discrepancy, viz. the surface roughness of the scaffold and the presence of micropores in the scaffold struts, was investigated with a view to making recommendations on improving FE model configurations for accurate effective property predictions.3

Purpose: Selective laser sintering (SLS) is a rapid pro- totyping technique applied to produce tissue-engineer- ing scaffolds from powder materials. The standard scanning technique, however, often produces struts of extensive thickness, which means fabrication of high- ly porous scaffolds with small overall dimensions is quite difficult. Nevertheless, this study aims to overcome this shortfall. Design/methodology/approach: To this end, three scanning methods were evaluated in terms of minimum feature size and freedom of design, using a test polyamide (PA) material. Polycaprolactone (PCL) was then employed to create highly porous 3D scaffolds using the preferred scanning me- thod to produce thin struts. Findings: While in normal scanning mode some features were well above the laser spot diameter, strut thicknesses below the laser spot diameter were achieved when using the “outline scan” function for PA material. Those achieved for PCL were slightly higher and in the 500-800 ?m range, with an average pore size of 400 µm. Investigations on the properties of the scaffolds revealed an effective compression modulus of the PCL scaffold of 6.5 MPa. Furthermore, there was no change in physical or che- mical properties when the scaffolds were stored in a physiological environment for 7 weeks. Originality/ value: Though SLS is considered as a fabrication te- chnique for tissue engineering scaffolds, actually pro- duced scaffolds did not comply with porosity requirements and limitations of the SLS process in produ- cing features at the size of the laser beam spot have not been discussed. The present paper shows the capabilities of the SLS process based on two materials and presents a method to minimize feature size in scaffolds

In bone tissue engineering, both geometrical and mechanical properties of a scaffold play a major part in the success of the treatment. The mechanical stresses and strains that act on cells on a scaffold in a physiological environment are a determining factor on the subsequent tissue formation. Computational models are often used to simulate the effect of changes of internal architectures and external loads applied to the scaffold in order to optimise the scaffold geometry for the prospective implantation site. Finite element analysis (FEA) based on computer models of the scaffold is a common technique, but would not take into account actual inaccuracies due to the manufacturing process. Image based FEA using CT scans of fabricated scaffolds can provide a more accurate analysis of the scaffold, and was used in this work in order to accurately simulate and predict the mechanical performance of bone tissue engineering scaffolds, fabricated using selective laser sintering (SLS), with a view to generating a methodology that could be used to optimise scaffold design. The present work revealed that an approach that assumes isotropic properties of SLS fabricated scaffolds will lead to inaccurate predictions of the FE model. However, a dependency of the grey value of the CT scans and the mechanical properties was discovered, which may ultimately lead to accurate FE models without the need of experimental validation.

No abstract