No abstract

A polyhedral oligomeric silsesquioxane (POSS), consisting mainly of a mixture of octahedra, nonahedra, and decahedra with bulky and flexible organic substituents, with three secondary hydroxyls per organic group, was used to modify epoxy networks produced by the homopolymerization of diglycidyl ether of bisphenol A in the presence of benzyldimethylamine. Several physical, thermal, and mechanical properties of the cured materials containing 0, 10, 30, and 50 wt % POSS were determined. The addition of POSS increased the elastic modulus and the yield stress measured in uniaxial compression tests, mainly because of the increase in the cohesive energy density produced by hydrogen bonding through the hydroxyl groups. A constant yield stress/elastic modulus ratio equal to 0.03 was observed for different POSS concentrations and test temperatures. The glass‐transition temperature decreased with POSS addition because of the flexibility of organic branches present in the POSS structure and the decrease in the crosslink density (determined from the rubbery modulus). Although a combination of a reduction in the glass‐transition temperature (plasticization) with an increase in the glassy modulus (antiplasticization) is a well‐known phenomenon, what is original is that in this case it was not the result of the suppression (or reduction in intensity) of subglass relaxations but was produced by an increase in the cohesive energy density. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1451–1461, 2003

One strategy for minimising corrosive attack on carbon steel involves the application of hybrid coatings rich in rare earths, on the basis of their low toxicity and environmental sustainability. Tetraethoxysilane (TEOS) and 3-glycidoxypropyl-trimethoxysilane (GPTMS) were each used here as precursors, together with various quantities of colloidal silica suspension, to improve barrier properties of the coatings. Ce(NO3)(3)center dot 6H(2)O was added as a source of Ce(III) for further inhibition of corrosion. The corrosion resistance of each kind of sample was evaluated using potentiodynamic polarisation measurements and electrochemical impedance spectroscopy (EIS) in 0.35 wt.% NaCI solution. The electrochemical behaviour at various immersion times was modelled by equivalent circuits to demonstrate the effect of silica nanoparticle loading on corrosion. Additional testing was performed under harsh conditions of salt spray chamber. The microstructure and composition of sol-gel coatings were characterised by scanning electron microscopy and energy dispersive X-ray spectroscopy (SEM/EDS), focused-ion beam SEM/EDS analysis, X-ray photoelectron spectroscopy and confocal microscopy. (C) 2015 Elsevier B.V. All rights reserved.Postprint (published version