Hollow hard shell particles of 200 nm and 2 micron diameter with a 10 nm thick porous silica shell have been synthesized using polystyrene templates and a sol–gel process. The template ensures than the hollow particles are monodispersed, while the charged silica surface ensures that they remain suspended in solution for weeks. When filled with perfluorocarbon gas, the particles behave as an efficient contrast agent for colour Doppler ultrasound imaging in human breast tissue. The silica shell provides unique properties compared to conventional soft shell particles employed as ultrasound contrast agents: uniform size control, strong adsorption to tissue and cells immobilizing particles at the tissue injection site, a long imaging lifetime, and a silica surface that can be easily modified with biotargeting ligands or small molecules to adjust the surface charge and polarity.

A novel design is demonstrated for a solid state, reagent-less sensor capable of rapid and simultaneous measurement of pH and Total Alkalinity (A) using ion sensitive field effect transistor (ISFET) technology to provide a simplified means of characterization of the aqueous carbon dioxide system through measurement of two "master variables": pH and A. ISFET-based pH sensors that achieve 0.001 precision are widely used in various oceanographic applications. A modified ISFET is demonstrated to perform a nanoliter-scale acid-base titration of A in under 40 s. This method of measuring A, a Coulometric Diffusion Titration, involves electrolytic generation of titrant, H, through the electrolysis of water on the surface of the chip via a microfabricated electrode eliminating the requirement of external reagents. Characterization has been performed in seawater as well as titrating individual components (i.e., OH, HCO, CO, B(OH), PO) of seawater A. The seawater measurements are consistent with the design in reaching the benchmark goal of 0.5% precision in A over the range of seawater A of ∼2200-2500 μmol kg which demonstrates great potential for autonomous sensing.

A simple method to fabricate Eu(3+) doped silica nanoshells particles with 100 and 200 nm diameters is reported. Amino polystyrene beads were used as templates, and an 8 to 10 nm thick silica gel coating was formed by the sol-gel reaction. After removing the template by calcination, porous dehydrated silica gel nanoshells of uniform size were obtained. The Eu(3+) doped silica nanoshells exhibited a red emission at 615 nm on UV excitation. The porous structure of the silica shell wall was characterized by transmission electron microscopy measurements, while particle size and zeta potentials of the particles suspended in aqueous solution were characterized by dynamic light scattering. Two-photon microscopy was used to image the nanoshells after assimilation by HeLa cancer cells.

A simple scalable method to fabricate luminescent monodisperse 200 nm europium doped hollow TiO2 nanoshell particles is reported. Fluorophore reporter, Eu3+ ions, are incorporated directly in the NS matrix, leaving the surface free for functionalization and the core free for payload encapsulation. Amine functionalized polystyrene beads were used as templates, and the porous walls of europium doped titania nanoshells were synthesized using titanium(IV) t-butoxide and europium(III) nitrate as reactants. X-ray diffraction analysis identified anatase as the predominant titania phase of the rigid nanoshell wall structure, and photoluminescence spectra showed that the Eu(III) doped TiO2 nanoshells exhibited a red emission at 617 nm due to an atomic f-f transition. Nanoshell interactions with HeLa cervical cancer cells in vitro were visualized using two-photon microscopy of the Eu(III) emission, and studied using a luminescence ratio analysis to assess nanoshell adhesion and endocytosis.