Solid-state low molecular temperature. Synopsispolymerization of poly(ethy1ene terephthalate) (PET) is carried out by heating the weight prepolymer at temperatures below its melting point but above its glass transition Postcondensation occurs and the condensation byproducts can be removed by applying vacuum or inert gas. Polymers obtained usually have high molecular weight, low carboxyl and acetaldehyde content, and can be used for beverage bottle or industrial yarns. Polyesters for textile purposes are manufactured by a melt process. Chemical reactions involved in the solid state polymerization are transesterification, esterification, as well as the diffusion of byproducts. Overall reaction rate was governed by the molecular weight, carboxyl content of prepolymer, crystallinity, particle size, reaction temperature, and time. Prepolymer for solid state polymerization should have intrinsic viscosity 0.4 dL/g or more, density 1.38 g/mL, and minimum dimension 3 mm or less. The reaction temperature could be 200-250OC. When textile grade PET is used as prepolymer, crystallization at 180-190°C for 1-2 b increases the density to 1.38 g/mL. Polymerization at 240-245°C for 3-5 h can raise the intrinsic viscosity to 0.72 dL/g and carboxyl content less than 20 meqkg. Appropriate reaction conditions are subject to the properties of prepolymers and the'design of reactors. Reactor used for solid state polymerization could be vacuum dryer type or stationary bed. The former is suitable for a small capacity and is run batchwise. The latter is a continuous process and is economically feasible for large-scale production.