PURPOSE: This study evaluated the degree of conversion (DC) of four indirect resin composites (IRCs) with various compositions processed in different polymerization units and investigated the effect of thermal aging on the flexural strength and Vicker's microhardness. MATERIALS AND METHODS: Specimens were prepared from four IRC materials, namely Gr 1: Resilab (Wilcos); Gr2: Sinfony (3M ESPE); Gr3: VITA VMLC (VITA Zahnfabrik); Gr4: VITA Zeta (VITA Zahnfabrik) using special molds for flexural strength test (N = 80, n = 10 per group) (25 x 2 x 2 mm(3), ISO 4049), for Vicker's microhardness test (N = 80, n = 10 per group) (5 x 4 mm(2)) and for DC (N = 10) using FT-Raman Spectroscopy. For both flexural strength and microhardness tests, half of the specimens were randomly stored in distilled water at 37 degrees C for 24 hours (Groups 1 to 4), and the other half (Groups 5 to 8) were subjected to thermocycling (5000 cycles, 5 to 55 +/-1 degree C, dwell time: 30 seconds). Flexural strength was measured in a universal testing machine (crosshead speed: 0.8 mm/min). Microhardness test was performed at 50 g. The data were analyzed using one-way and two-way ANOVA and Tukey's test (alpha= 0.05). The correlation between flexural strength and microhardness was evaluated with Pearson's correlation test (alpha= 0.05). RESULTS: A significant effect for the type of IRC and thermocycling was found (p= 0.001, p= 0.001) on the flexural strength results, but thermocycling did not significantly affect the microhardness results (p= 0.078). The interaction factors were significant for both flexural strength and microhardness parameters (p= 0.001 and 0.002, respectively). Thermocycling decreased the flexural strength of the three IRCs tested significantly (p < 0.05), except for VITA Zeta (106.3 +/-9.1 to 97.2 +/-14 MPa) (p > 0.05) when compared with nonthermocycled groups. Microhardness results of only Sinfony were significantly affected by thermocycling (25.1 +/-2.1 to 31 +/-3.3 Kg/mm(2)). DC values ranged between 63% and 81%, and were not significantly different between the IRCs (p > 0.05). While a positive correlation was found between flexural strength and microhardness without (r = 0.309) and with thermocycling (r = 0.100) for VITA VMLC, negative correlations were found for Resilab under the same conditions (r =-0.190 and -0.305 AbstractPurpose: This study evaluated the degree of conversion (DC) of four indirect resin composites (IRCs) with various compositions processed in different polymerization units and investigated the effect of thermal aging on the flexural strength and Vicker's microhardness. Materials and Methods: Specimens were prepared from four IRC materials, namely Gr 1: Resilab (Wilcos); Gr2: Sinfony (3M ESPE); Gr3: VITA VMLC (VITA Zahnfabrik); Gr4: VITA Zeta (VITA Zahnfabrik) using special molds for flexural strength test (N = 80, n = 10 per group) (25 × 2 × 2 mm 3 , ISO 4049), for Vicker's microhardness test (N = 80, n = 10 per group) (5 × 4 mm 2 ) and for DC (N = 10) using FT-Raman Spectroscopy. For both fle...

The RS finish line produced MD values significantly lower than tilted and large chamfer, but large chamfer presented the lowest internal discrepancy values. Independent of the finish line type, internal discrepancy was the lowest in the axial region followed by radius and occlusal regions.

Air-particle abrasion with Al(2)O(3) improved the shear bond strength between metal and ceramics used.

After NVB, adhesive luting to dentin is recommended after 7 days if sodium ascorbate has been applied prior to dentin hybridization.

The aim of this study was to evaluate the effects of different light-curing units and resin cement curing types on the bond durability of a feldspathic ceramic bonded to dentin. The crowns of 40 human molars were sectioned, exposing the dentin. Forty ceramic blocks of VITA VM7 were produced according to the manufacturer's recommendations. The ceramic surface was etched with 10% hydrofluoric acid / 60s and silanized. The dentin was treated with 37% phosphoric acid / 15s, and the adhesive was applied. The ceramic blocks were divided and cemented to dentin according to resin cement / RC curing type (dual-and photocured), light-curing unit (halogen light / QTH and LED), and storage conditions (dry and storage / 150 days + 12,000 cycles / thermocycling). All blocks were stored in distilled water (37°C / 24h) and sectioned (n = 10): G1 -QTH + RC Photo, G2 -QTH + RC Dual, G3 -LED + RC Photo, G4 -LED + RC Dual. Groups G5, G6, G7, and G8 were obtained exactly as G1 through G4, respectively, and then stored and thermocycled. Microtensile bond strength tests were performed (EMIC), and data were statistically analyzed by ANOVA and Tukey's test (5%). The bond strength values (MPa) were: G1 -12.95 (6.40) ab ; G2 -12.02 (4.59) ab ; G3 -13.09 (5.62) ab ; G4 -15.96 (6.32) a ; G5 -6.22 (5.90) c ; G6 -9.48 (5.99) bc ; G7 -12.78 (11.30) ab ; and G8 -8.34 (5.98) bc . The same superscript letters indicate no significant differences. Different light-curing units affected the bond strength between ceramic cemented to dentin when the photocured cement was used, and only after aging (LED > QTH). There was no difference between the effects of dual-and photo-cured resin-luting agents on the microtensile bond strength of the cement used in this study.