There is an interest in the sustainable utilization of waste cotton cloths because of their enormous volume of generation and high cellulose content. Waste cotton cloths generated are disposed of in a landfill, which causes environmental pollution and leads to the waste of useful resources. In the present study, cellulose nanocrystals (CNCs) were isolated from waste cotton cloths collected from a landfill. The waste cotton cloths collected from the landfill were sterilized and cleaned using supercritical CO2 (scCO2) technology. The cellulose was extracted from scCO2-treated waste cotton cloths using alkaline pulping and bleaching processes. Subsequently, the CNCs were isolated using the H2SO4 hydrolysis of cellulose. The isolated CNCs were analyzed to determine the morphological, chemical, thermal, and physical properties with various analytical methods, including attenuated total reflection-Fourier transform-infrared spectroscopy (ATR-FTIR), field-emission scanning electron microscopy (FE-SEM), energy-filtered transmission electron microscopy (EF-TEM), X-ray diffraction (XRD), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). The results showed that the isolated CNCs had a needle-like structure with a length and diameter of 10-30 and 2-6 nm, respectively, and an aspect ratio of 5–15, respectively. Additionally, the isolated CNCs had a high crystallinity index with a good thermal stability. The findings of the present study revealed the potential of recycling waste cotton cloths to produce a value-added product.

In the present study, supercritical carbon dioxide (scCO2) was utilized as a waterless pulping for the isolation of cellulose nanocrystals (CNCs) from waste cotton cloths (WCCs). The isolation of CNCs from the scCO2-treated WCCs’ fiber was carried out using sulphuric acid hydrolysis. The morphological and physicochemical properties analyses showed that the CNCs isolated from the WCCs had a rod-like structure, porous surface, were crystalline, and had a length of 100.03 ± 1.15 nm and a width of 7.92 ± 0.53 nm. Moreover, CNCs isolated from WCCs had a large specific surface area and a negative surface area with uniform nano-size particles. The CNCs isolated from WCCs were utilized as an adsorbent for the hexavalent chromium [Cr(VI)] removal from aqueous solution with varying parameters, such as treatment time, adsorbent doses, pH, and temperature. It was found that the CNCs isolated from the WCCs were a bio-sorbent for the Cr(VI) removal. The maximum Cr(VI) removal was determined to be 96.97% at pH 2, 1.5 g/L of adsorbent doses, the temperature of 60 °C, and the treatment time of 30 min. The adsorption behavior of CNCs for Cr(VI) removal was determined using isothermal, kinetics, and thermodynamics properties analyses. The findings of the present study revealed that CNCs isolated from the WCCs could be utilized as a bio-sorbent for Cr(VI) removal.

No abstract

No abstract