A novel class of surface-active copolymers is described, designed to protect surfaces from nonspecific protein adsorption while still inducing specific cell attachment and spreading. A graft copolymer was synthesized, containing poly-(L-lysine) (PLL) as the backbone and substrate binding and poly(ethylene glycol) (PEG) as protein adsorption-resistant pendant side chains. A fraction of the grafted PEG was pendantly functionalized by covalent conjugation to the peptide motif RGD to induce cell binding. The graft copolymer spontaneously adsorbs from dilute aqueous solution onto negatively charged surfaces. The performance of RGD-modified PLL-g-PEG copolymers was analyzed in protein adsorption and cell culture assays. These coatings efficiently blocked the adsorption of serum proteins to Nb(2)O(5) and tissue culture polystyrene while specifically supporting attachment and spreading of human dermal fibroblasts. This surface functionalization technology is expected to be valuable in both the biomaterial and biosensor fields, because different signals can easily be combined, and sterilization and application are straightforward and cost-effective.

No abstract

Osteoblasts exhibit a more differentiated morphology on surfaces with rough microtopographies. Surface effects are often mediated through integrins that bind the RGD motif in cell attachment proteins. Here, we tested the hypothesis that modulating access to RGD binding sites can modify the response of osteoblasts to surface microtopography. MG63 immature osteoblast-like cells were cultured on smooth (Ti sputter-coated Si wafers) and rough (grit blasted/acid etched) Ti surfaces that were modified with adsorbed monomolecular layers of a comb-like graft copolymer, poly-(L-lysine)-g-poly(ethylene glycol) (PLL-g-PEG), to limit nonspecific protein adsorption. PLL-g-PEG coatings were functionalized with varying amounts of an integrin-receptor-binding RGD peptide GCRGYGRGDSPG (PLL-g-PEG/PEG-RGD) or a nonbinding RDG control sequence GCRGYGRDGSPG (PLL-g-PEG/PEG-RDG). Response to PLL-g-PEG alone was compared with response to surfaces on which 2-18% of the polymer sidechains were functionalized with the RGD peptide or the RDG peptide. To examine RGD dose-response, peptide surface concentration was varied between 0 and 6.4 pmol/cm(2). In addition, cells were cultured on uncoated Ti or Ti coated with PLL-g-PEG or PLL-g-PEG/PEG-RGD at an RGD surface concentration of 0.7 pmol/cm(2), and free RGDS was added to the media to block integrin binding. Analyses were performed 24 h after cultures had achieved confluence on the tissue culture plastic surface. Cell number was reduced on smooth Ti compared to plastic or glass and further decreased on surfaces coated with PLL-g-PEG or PLL-g-PEG/PEG-RDG, but was restored to control levels when PLL-g-PEG/PEG-RGD was present. Alkaline phosphatase specific activity and osteocalcin levels were increased on PLL-g-PEG alone or PLL-g-PEG/PEG-RDG, but PLL-g-PEG/PEG-RGD reduced the parameters to control levels. On rough Ti surfaces, cell number was reduced to a greater extent than on smooth Ti. PLL-g-PEG coatings reduced alkaline phosphatase and increased osteocalcin in a manner that was synergistic with surface roughness. The RDG peptide did not alter the PLL-g-PEG effect but the RGD peptide restored these markers to their control levels. PLL-g-PEG coatings also increased TGF-beta1 and PGE(2) in conditioned media of cells cultured on smooth or rough Ti; there was a 20x increase on rough Ti coated with PLL-g-PEG. PLL-g-PEG effects were inhibited dose dependently by addition of the RGD peptide to the surface. Free RGDS did not decrease the effect elicited by PLL-g-PEG surfaces. These unexpected results suggest that PLL-g-PEG may have osteogenic properties, perhaps correlated with effects that alter cell attachment and spreading, and promote a more differentiated morphology.