We report the fabrication of high quality monolithically integrated optical long-pass filters, for use in disposable diagnostic microchips. The filters were prepared by incorporating dye molecules directly into the microfluidic chip substrate, thereby providing a fully integrated solution that removes the usual need for discrete optical filters. In brief, lysochrome dyes were added to a poly(dimethylsiloxane) (PDMS) monomer prior to moulding of the microchip from a structured SU-8 master. Optimum results were obtained using 1 mm layers of PDMS doped with 1200 microg mL(-1) Sudan II, which resulted in less than 0.01% transmittance below 500 nm (OD 4), >80% above 570 nm, and negligible autofluorescence. These spectral characteristics compare favourably with commercially available Schott-glass long-pass filters, indicating that high quality optical filters can be straightforwardly integrated into the form of PDMS microfluidic chips. The filters were found to be robust in use, showing only slight degradation after extended illumination and negligible dye leaching after prolonged exposure to aqueous solutions. The provision of low cost high quality integrated filters represents a key step towards the development of high-sensitivity disposable microfluidic devices for point-of-care diagnostics.

We fabricate a saturable absorber mirror by coating a graphene film on an output coupler mirror. This is then used to obtain Q-switched mode-locking from a diode pumped linear cavity waveguide laser inscribed in Ytterbium-doped Bismuthate Glass, with high slope and optical conversion efficiencies. The laser produces mode-locked pulses at∼1039nm, with 1.5GHz repetition rate at an average 202mW output power. This performance is due to the combination of the graphene saturable absorber with the high quality laser glass.

We report near-infrared (IR) to mid-IR (up to 3.4 μm wavelength) multimode waveguiding in deep buried channel waveguides fabricated inside rare-earth ion-doped ceramic YAG for the first time to our knowledge. Waveguide laser operation at around 2 μm wavelength with multi- or single-transverse modes is also preliminarily demonstrated from these waveguides.

Ultrafast laser inscription is used to fabricate the gain element for a mode-locked Er-doped bismuthate glass waveguide laser. Mode-locking is initiated and stabilized by the use of a single wall carbon nanotube saturable absorber. The waveguide laser produces 320 fs pulses at 1.56 m with a pulse repetition rate of 40 MHz and average output power of 1.25 mW.