Guided bone regeneration (GBR) procedures using graft materials have been used for reconstruction of osseous defects. The aim of the present in vivo micro-computed tomographic (µCT) and histologic study was to assess in real time the bone regeneration at GBR sites in standardized experimental calvarial defects (diameter 3.3 mm) using β-tricalcium phosphate (β-TCP) with and without collagen membrane (CM). A single full-thickness calvarial defect was created on the left parietal bone in young female Wistar albino rats (n = 30) weighing approximately 300 g and aged about 6 weeks. The animals were randomly divided into three groups for treatment, based on calvarial defect filling material: (1) control group (n = 10); (2) β-TCP + CM group (n = 10); (3) β-TCP group (n = 10). Real-time in vivo µCT analyses were performed immediately after surgery and at 2, 4, 6 and 10 weeks to determine the volume and mineral density of the newly formed bone (BVNFB, MDNFB) and remaining β-TCP particles (VRBP, MDRBP). The animals were killed at 10 weeks and calvarial specimens were evaluated histologically. In the control group, MDNFB increased significantly at 6 weeks (0.32 ± 0.002 g/mm(3), P < 0.01) compared to that at baseline. In β-TCP + CM group, BVNFB (1.10 ± 0.12 mm(3), P < 0.01) and MDNFB (0.13 ± 0.02 g/mm(3), P < 0.01) significantly increased at the 4th week than baseline. In the β-TCP group, BVNFB (1.13 ± 0.12 mm(3), P < 0.01) and MDNFB (0.14 ± 0.01 g/mm(3), P < 0.01) significantly increased at 6 weeks compared to that at baseline. Significant reduction in VRBP was neither seen in the β-TCP + CM group nor in the β-TCP group. While in the β-TCP + CM group MDRBP was reduced significantly at 6 weeks (0.44 ± 0.9 g/mm(3), P < 0.01) from baseline (0.98 ± 0.03 g/mm(3)), similar significant reduction in MDRBP from baseline (0.92 ± 0.07 g/mm(3)) was seen only at 10 weeks (0.45 ± 0.06 g/mm(3), P < 0.05) in the β-TCP group. Histologic findings at 10 weeks revealed greater amount of NFB with osteocytes in the matrix, in the β-TCP + CM group than in the β-TCP group. Biomechanical assessment of NFB for hardness (H) and elastic modulus (E) revealed significantly higher values for the β-TCP + CM group (H = 612.6 ± 4.28 Mpa; E = 13.57 ± 0.07 Gpa) when compared to those of the control (H = 192.1 ± 4.93 Mpa; E = 6.76 ± 0.04 Gpa) and the β-TCP groups (H = 241.9 ± 6.29 Mpa; E = 4.34 ± 0.06 Gpa). In conclusion, based on real-time assessment, NFB is formed in calvarial defects as early as 4 weeks following GBR with β-TCP + CM as compared to 6 weeks when β-TCP alone was used.
Based on the results of this study, perioperative oral antibiotics in combination with antibacterial mouthwashes are effective in preventing ORN following dental extractions in irradiated patients.
The aim of the present real time in vivo micro-computed tomography (µCT) and histologic experiment was to assess the efficacy of guided bone regeneration (GBR) around standardized calvarial critical size defects (CSD) using bone marrow-derived mesenchymal stem cells (BMSCs), and collagen membrane (CM) with and without tricalcium phosphate (TCP) graft material. In the calvaria of nine female Sprague-Dawley rats, full-thickness CSD (diameter 4.6 mm) were created under general anesthesia. Treatment-wise, rats were divided into three groups. In group 1, CSD was covered with a resorbable CM; in group 2, BMSCs were filled in CSD and covered with CM; and in group 3, TCP soaked in BMSCs was placed in CSD and covered with CM. All defects were closed using resorbable sutures. Bone volume and bone mineral density of newly formed bone (NFB) and remaining TCP particles and rate of new bone formation was determined at baseline, 2, 4, 6, and 10 weeks using in vivo µCT. At the 10th week, the rats were killed and calvarial segments were assessed histologically. The results showed that the hardness of NFB was similar to that of the native bone in groups 1 and 2 as compared to the NFB in group 3. Likewise, values for the modulus of elasticity were also significantly higher in group 3 compared to groups 1 and 2. This suggests that TCP when used in combination with BMSCs and without CM was unable to form bone of significant strength that could possibly provide mechanical “lock” between the natural bone and NFB. The use of BMSCs as adjuncts to conventional GBR initiated new bone formation as early as 2 weeks of treatment compared to when GBR is attempted without adjunct BMSC therapy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.