Magnetic nanoparticles are the functional component for magnetic membranes, but they are difficult to disperse and process into tough membranes. Here, cellulose nanofibers are decorated with magnetic ferrite nanoparticles formed in situ which ensures a uniform particle distribution, thereby avoiding the traditional mixing stage with the potential risk of particle agglomeration. The attachment of the particles to the nanofibrils is achieved via aqueous in situ hydrolysis of metal precursors onto the fibrils at temperatures below 100 C. Metal adsorption and precursor quantification were carried out using Induction Coupled Plasma-Optical Emission Spectroscopy (ICP-OES). FE-SEM was used for high resolution characterization of the decorated nanofibers and hybrid membranes, and TEM was used for nanoparticle size distribution studies. The decorated nanofibers form a hydrocolloid. Large (200 mm diameter) hybrid cellulose/ferrite membranes were prepared by simple filtration and drying of the colloidal suspension. The low-density, flexible and permanently magnetized membranes contain as much as 60 wt% uniformly dispersed nanoparticles (thermogravimetric analysis data). Hysteresis magnetization was measured by a Vibrating Sample Magnetometer; the inorganic phase was characterized by XRD. Membrane mechanical properties were measured in uniaxial tension. An ultrathin prototype loudspeaker was made and its acoustic performance in terms of output sound pressure was characterized. A full spectrum of audible frequencies was resolved.

Moisture stability and brittleness are challenges for plant fiber biocomposites intended for load-bearing applications, for instance those based on an amylopectin-rich (AP) starch matrix. Core-shell amylopectin-coated cellulose nanofibers and nanocomposites are prepared to investigate effects from the distribution of AP matrix. The core-shell nanocomposites are compared with nanocomposites with more irregular amylopectin (AP) distribution. Colloidal properties (DLS), AP adsorption, nanofiber dimensions (atomic force microscopy), and nanocomposite structure (transmission electron microscopy) are analyzed. Tensile tests are performed at different moisture contents. The core-shell nanofibers result in exceptionally moisture stable, ductile, and strong nanocomposites, much superior to reference CNF/AP nanocomposites with more irregular AP distribution. The reduction in AP properties is less pronounced as the AP forms a favorable interphase around individual CNF nanofibers.