This paper presents the results of an interlaboratory study of the rheological properties of cement paste and ultrasound gel as reference substance. The goal was to quantify the comparability and reproducibility of measurements of the Bingham parameters yield stress and plastic viscosity when measured on one specific paste composition and one particular ultrasound gel in different laboratories using

Flowable concretes tend to segregate. The risk of segregation is particularly high when the concrete is vibrated during the compaction process. A well-known segregation phenomenon is the so-called “bleeding”. This is a rise of water to the surface of the freshly poured concrete due to the difference in density between the mixing water and the concrete’s denser solid components (aggregates, cement and additives). This type of segregation occurs particularly within the paste. The focus of this paper is, therefore, on the sedimentation behavior at the microscale of concrete and especially on the influence of this process on rheological properties of the cement paste. In addition to common bleeding tests of cement suspensions using standing cylinders, rheometric measurements were performed on the suspensions during the bleeding process. A measuring procedure was developed for the rheometric measurements of the sedimenting cement suspensions. The rheological properties of the investigated cement suspensions were determined at four specific measuring times and at four specific measuring heights (i.e., positions) each. With this method it could be shown that the cement suspensions are not homogeneous over their height and that bleeding has a great influence on the rheological properties of cement suspension.

The impact of low-pressure treatment on the crystal structure, morphology, and chemical composition of ettringite, due to their major importance with respect to processability (i.a., drying conditions) and to the analysis of ettringite-containing samples, is examined utilizing X-ray diffraction, thermogravimetric analysis, Raman spectroscopy, and environmental scanning electron microscopy. Synthetic ettringite was treated for various durations (5 min up to 72 h) and at two different levels of low-pressure (4.0 mbar and 60 µbar). Evaluation showed a correlation between the procedural parameters (time and pressure), the chemical composition, and the morphology of ettringite. The experiments reveal that, when exposed to 4 mbar pressure, nearly no changes occur in the ettringite’s morphology, whereas the crystals undergo swelling and slight deformations at very low pressures (60 µbar and 35.3 nbar), which is attributed to the loss of bound water and the partial transformation from ettringite to quicklime, anhydrite, and calcium aluminate. Furthermore, the strongly dehydrated ettringite shows the same morphology.

No abstract

No abstract