ABSTRACT3D woven composites reinforced with either S2 glass, carbon or a hybrid combination of both and containing either polyethylene or carbon z-yarns were tested under low-velocity impact. Different impact energies (in the range of 21-316 J) were used and the mechanical response (in terms of the impact strength and energy dissipated) was compared with that measured in high-performance, albeit standard, 2D laminates. It was found that the impact strength in both 2D and 3D materials was mainly dependent on the in-plane fiber fracture. Conversely, the energy absorption capability was primarily influenced by the presence of z-yarns, having the 3D composites dissipated over twice the energy than the 2D laminates, irrespective of their individual characteristics (fiber type, compaction degree, porosity, etc.). X-ray microtomography revealed that this improvement was due to the z-yarns, which delayed delamination and maintained the structural integrity of the laminate, promoting energy dissipation by tow splitting, intensive fiber breakage under the tup and formation of a plug by out-of-plane shear.

This is a PDF file of an article that has undergone enhancements after acceptance, such as the addition of a cover page and metadata, and formatting for readability, but it is not yet the definitive version of record. This version will undergo additional copyediting, typesetting and review before it is published in its final form, but we are providing this version to give early visibility of the article. Please note that, during the production process, errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal pertain.