Planar perovskite solar cells (PSCs) made entirely via solution processing at low temperatures (<150°C) offer promise for simple manufacturing, compatibility with flexible substrates, and perovskite-based tandem devices. However, these PSCs require an electron-selective layer that performs well with similar processing. We report a contact-passivation strategy using chlorine-capped TiO colloidal nanocrystal film that mitigates interfacial recombination and improves interface binding in low-temperature planar solar cells. We fabricated solar cells with certified efficiencies of 20.1 and 19.5% for active areas of 0.049 and 1.1 square centimeters, respectively, achieved via low-temperature solution processing. Solar cells with efficiency greater than 20% retained 90% (97% after dark recovery) of their initial performance after 500 hours of continuous room-temperature operation at their maximum power point under 1-sun illumination (where 1 sun is defined as the standard illumination at AM1.5, or 1 kilowatt/square meter).

Perovskite solar cells (PSCs) have witnessed rapidly rising power conversion efficiencies, together with advances in stability and upscaling. Despite these advances, their limited stability and need to prove upscaling remain crucial hurdles on the path to commercialization. We summarize recent advances toward commercially viable PSCs and discuss challenges that remain. We expound the development of standardized protocols to distinguish intrinsic and extrinsic degradation factors in perovskites. We review accelerated aging tests in both cells and modules and discuss the prediction of lifetimes on the basis of degradation kinetics. Mature photovoltaic solutions, which have demonstrated excellent long-term stability in field applications, offer the perovskite community valuable insights into clearing the hurdles to commercialization.

No abstract