Solid oxide fuel cell (SOFC) electrode materials with surface areas up to 99 m 2 • g −1 were prepared at traditional sintering temperatures, 1050 • C-1350 • C, by sintering hybrid inorganic-organic materials in an inert atmosphere followed by calcination in air at 700 • C. The electrode materials investigated were yttria-stabilized zirconia (YSZ), lanthanum strontium cobalt ferrite (LSCF), gadolinia doped ceria (GDC), and strontium titanate (STO). During sintering, an amorphous carbon template forms in situ and remains throughout the sintering process, aiding in the creation and preservation of mixed-metal-oxide nanomorphology. The carbon template is removed during subsequent calcination in air at 700 • C, leaving behind a nanostructured ceramic. Phase stability, carbon template concentration, and specific surface area was determined for each mixed-metal-oxide. Final specific surface areas up to 83, 66, 95, and 99 m 2 • g −1 were achieved for YSZ, LSCF, GDC, and STO, respectively. The impact of high surface area YSZ on symmetrical YSZ-lanthanum strontium ferrite (LSF) cathode cell performance was evaluated in the temperature range of 550 • C-800 • C. Adding nanostructured YSZ decreased the electrochemical impedance by 45% at 550 • C. The performance improvement lessened with increasing temperature, and at 800 • C there was essentially no improvement. The findings reveal a promising approach to improving low temperature SOFC performance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.