The O‐phospho‐L‐serine [Ser(P)] containing peptides and proteins play an important role in controlling the morphology of biominerals. The poly[Ser(P)] and copoly[Ser(P)xAspy] affect the calcium carbonate (CaCO3) morphology and polymorph. The CaCO3 helical structures were obtained in the presence of copoly[Ser(P)75Asp25]. When the L‐copolymer was used as an additive, a clockwise P twisted spiral morphology was formed. On the other hand, when using D‐copolymer, a counterclockwise M twisted spiral morphology was obtained.

The modification of CaCO(3) crystal growth by synthetic L-Ser(PO(3)H(2)) and L-Thr(PO(3)H(2)) containing polypeptides is described. The amino acids Gly, L-Glu, L-Asp, L-Ser, L-Ala, and L-Lys induced rhombohedral calcite with a rough surface. Dipeptides, Xaa-L-Ser(PO(3)H(2)) (Xaa = Gly, L-Glu, L-Asp, L-Ser, L-Ala and L-Lys) induced vaterite crystals in the lower [Ca(2+)]. On the other hand, L-Ser(PO(3)H(2))-containing polypeptides formed spherical vaterite and fibrous calcite. The characteristic helical calcite was found in the presence of copoly[L-Ser(PO(3)H(2))(75)L-Asp(25)] or poly[L-Ser(PO(3)H(2))(3)-L-Asp]. Fibrous calcite, spherical vaterite, and helical calcite crystals were subjected to XRD and EDX analysis. XRD revealed the specific faces of these crystals. EDX spectra and surface analysis visualized the localization of the polypeptides and CaCO(3) components. Together with TEM and SAED data, we propose hypothetical growth mechanisms for the fibrous and helical calcite crystals.

No abstract

It is important to match the feeding ratio of comonomers to the composition ratio in the resulting copolymers as closely as possible in industrial production, where the goal is often to produce more a homogeneous composition in copolymers. In this study, a flow copolymerization system with a conventionally initiated free radical method, together with randomly selected polymerization conditions is investigated. It is succeeded in achieving a closer match between the composition ratio and feeding ratio than previously reported in the copolymerization of styrene with methyl methacrylate and of glycidyl methacrylate with methyl methacrylate, which will widen the range of applications, by precisely controlling the mixing and heating in a flow polymerization apparatus. This is confirmed by the fact that the estimated values of reactivity ratios, r 1 and r 2 , which are used in the reaction kinetics of copolymerization, are close to 1.

The properties of polymers are highly dependent on the combination and composition ratio of the monomers used to prepare them; however, the large number of available monomers makes an exhaustive...