Aim To evaluate possible modifications in root canal sealers subjected to a variety of heating conditions using vibrational spectroscopy and analysis of physical and chemical properties. Methodology EndoSequence BC Sealer HiFlow, Bio‐C Sealer, BioRoot RCS and AH Plus were analysed chemically using Raman spectroscopy (25–220 °C) and Fourier‐transform infrared spectroscopy (FT‐IR) (37–100 °C ). For FT‐IR, the materials were tested individually and mixed with root dentine powder. Scanning electron microscopy (SEM) and coupled energy dispersive spectroscopy (EDS) were used to evaluate surface and chemical elements. ISO 6876‐2012 and ASTM‐C266‐07 specifications were followed to evaluate flow, setting time (moist and dry), solubility and radiopacity. Also, pH analysis at 37 and 100 °C was performed. Shapiro–Wilk and Mixed ANOVA (within and between the effects of the subjects), Levene, and a post hoc analyses with Bonferroni correction were performed (P < 0.05). Results Vibrational spectroscopy revealed peaks of tricalcium silicate, dicalcium silicate and zirconium dioxide. Chemical changes in the Raman spectra during heating were discrete, as the inorganic content predominated the signalling for all root canal sealers. FT‐IR analysis exhibited spectral changes in water absorption for EndoSequence BC Sealer HiFlow and Bio‐C Sealer, probably related to dehydration. For BioRoot RCS and AH Plus, no significant chemical changes were observed. Bio‐C Sealer exhibited a band of polyethylene glycol only after heating to 100 °C, probably related to its thermal decomposition. SEM/EDS analysis corroborated the composition results observed in vibrational spectroscopy for all materials. Heating to 100 °C significantly changed the flowability of all calcium silicate‐based sealers with a wide variation in setting times at both temperatures, along with solubility levels above ISO standards. For all tested sealers, radiopacity fulfilled the requirements, and pH exhibited alkaline values. Conclusions The tested calcium silicate‐based sealers were affected by heating. Calcium silicate‐based root canal sealers had high solubility which is a concern for their clinical use. AH Plus was the only root canal sealer that was stable after heating.

Where a licence is displayed above, please note the terms and conditions of the licence govern your use of this document.When citing, please reference the published version. Take down policyWhile the University of Birmingham exercises care and attention in making items available there are rare occasions when an item has been uploaded in error or has been deemed to be commercially or otherwise sensitive.

This study evaluated the physicochemical, biological, and antimicrobial properties of a new hydraulic calcium silicate-based modified material, and compared it with MTA Repair HP and MTA Angelus. The materials were assessed regarding color luminosity (L), color change, radiopacity, setting time, and ISO 6876:2012 linear flow. Volumetric filling and volume change were evaluated using microcomputed-tomography (µCT). Chemical characterization after 28 days in Hank's Balanced Salt Solution (HBSS) and pH analysis were also assessed. Biological characterization of cytotoxicity and microbiological assessment were also undertaken. Shapiro-Wilk, ANOVA, Levene and post hoc analyses with Bonferroni correction were performed, adopting a 5% significance level (p <0.05). Bio-C Pulpo exhibited the highest L values after 90 days. All tested materials demonstrated color change during the analyses, and had radiopacity above 5 mm Al. MTA Repair HP set faster than Bio-C Pulpo, whereas the latter had the highest linear flow. MTA Repair HP had the highest volumetric filling in µCT analysis. Bio-C Pulpo showed the highest alkalinity during all tested periods, and the highest volumetric loss (above 9%), in comparison with MTA Repair HP and MTA Angelus. Bio-C Pulpo did not form calcium hydroxide after hydration. MTA Repair HP demonstrated the highest cytocompatibility, and Bio-C Pulpo, the highest cytotoxicity. No inhibition halos were observed for any material, and similar higher turbidity values were seen after direct contact. Composition additives used in Bio-C Pulpo modified its properties, and both the absence of calcium hydroxide deposition after hydration, and the related cytotoxicity of this material are of particular concern.

Objectives: This study evaluated the bond strength of various fiberglass post cementation techniques using different resin-based composites. Materials and Methods: The roots from a total of 100 bovine incisors were randomly assigned to 5 treatment groups: G1, post + Scotchbond MultiPurpose (SBMP) + RelyX ARC luting agent; G2, relined post (Filtek Z250) + SBMP + RelyX ARC; G3, individualized post (Filtek Z250) + SBMP; G4, individualized post (Filtek Bulk-Fill) + SBMP; G5, individualized post (Filtek Bulk-Fill Flow) + SBMP. The samples were subjected to the push-out (n = 10) and pull-out (n = 10) bond strength tests. Data from the push-out bond strength test were analyzed using 2-way analysis of variance (ANOVA) with the Bonferroni post hoc test, and data from the pull-out bond strength test were analyzed using 1-way ANOVA. Results: The data for push-out bond strength presented higher values for G2 and G5, mainly in the cervical and middle thirds, and the data from the apical third showed a lower mean push-out bond strength in all groups. No significant difference was noted for pull-out bond strength among all groups. The most frequent failure modes observed were adhesive failure between dentine and resin and mixed failure. Conclusions: Fiberglass post cementation using restorative and flowable bulk-fill composites with the individualization technique may be a promising alternative to existing methods of post cementation.

The substitution of calcium with strontium in bioactive materials has been promising but there has been some concern over the material instability and possible toxicity. The aim of this research was the synthesis and characterization of calcium and strontium substituted bioactive materials and assessment of interactions with local tissues and peripheral elemental migration in an animal model. A bioactive glass, hydroxyapatite and hydraulic calcium silicate with 50% or 100% calcium substitution with strontium were developed and the set materials were characterized immediately after setting and after 30 and 180-days in solution.Following subcutaneous implantation, the local (tissue histology, elemental migration) and systemic effects (elemental deposition after organ digestion) were assessed. The strontium-replaced silicate cements resulted in the synthesis of partially substituted phases and strontium leaching at all-time points. The strontium silicate implanted in the animal model could not be retrieved in over half of the specimens showing the high rate of material digestion. Tissue histology showed that all materials caused inflammation after 30 days of implantation however this subsided and angiogenesis occurred after 180 days. Strontium was not detected in the local tissues or the peripheral organs while all calcium containing materials caused calcium deposition in the kidneys. The tricalcium silicate caused elemental migration of calcium and silicon in the local tissues shown by the elemental mapping but no deposition of calcium was identified in the peripheral organs verified by the assessment of the digested tissues. Strontium can substitute calcium in bioactive materials without adverse local or systemic effects.