Background Aseptic loosening continues to be a shortand long-term complication for patients with cemented TKAs. Most studies to this point have evaluated tibial component fixation via radiographic changes at the implant-bone interface and quantification of component migration; direct assessment of morphologic features of the interface from functioning TKAs may provide new information regarding how TKAs function and are fixed to bone. Questions/purposes In a postmortem retrieval study, we asked: (1) What are the morphologic features at the cement-trabecular bone interface in retrieved tibial components? (2) Do constructs with greater time in service have less cement-trabecular bone interlock? (3) Do constructs with more estimated initial interlock sustain more interlock with in vivo service? Methods Fourteen postmortem retrieved tibial components with time in service from 0 to 20 years were sectioned and imaged at high resolution, and the current contact fraction, estimated initial interdigitation depth, current interdigitation depth, and loss of interdigitation depth were quantified at the cement-bone interface. Estimated initial interdigitation depth was calculated from the initial mold shape of the cement mantle that forms around the individual trabeculae at the time of surgery. Loss of interdigitation depth was the difference between the initial and current interdigitation depth. Results There was resorption of trabeculae that initially interlocked with the cement in the postmortem retrievals as evidenced by the differences between current interdigitation and the estimated original interdigitation. The current contact fraction (r 2 = 0.54; p = 0.0027) and current interdigitation depth (r 2 = 0.33; p = 0.033) were less for constructs with longer time in service. The current contact fraction for implants with 10 or more years in service (6.2%; 95% CI, 4.7%-7.7%) was much less than implants with less than 10 years in service (22.9%; 95% CI, 8.9%-37%). Similarly, the current interdigitation depth for implants with 10 or more years in service (0.4 mm; 95% CI, 0.27-0.53 mm) was much less than implants with less
Background and purposeDespite the longstanding use of micromotion as a measure of implant stability, direct measurement of the micromechanics of implant/bone interfaces from en bloc human retrievals has not been performed. The purpose of this study was to determine the stem-cement and cement-bone micromechanics of functionally loaded, en-bloc retrieved, cemented femoral hip components.Methods11 fresh frozen proximal femurs with cemented implants were retrieved at autopsy. Specimens were sectioned transversely into 10-mm slabs and fixed to a loading device where functional torsional loads were applied to the stem. A digital image correlation technique was used to document micromotions at stem-cement and cement-bone interfaces during loading.ResultsThere was a wide range of responses with stem-cement micromotions ranging from 0.0006 mm to 0.83 mm (mean 0.17 mm, SD 0.29) and cement-bone micromotions ranging from 0.0022 mm to 0.73 mm (mean 0.092 mm, SD 0.22). There was a strong (linear-log) inverse correlation between apposition fraction and micromotion at the stem-cement interface (r2 = 0.71, p < 0.001). There was a strong inverse log-log correlation between apposition fraction at the cement-bone interface and micromotion (r2 = 0.85, p < 0.001). Components that were radiographically well-fixed had a relatively narrow range of micromotions at the stem-cement (0.0006–0.057 mm) and cement-bone (0.0022–0.029 mm) interfaces.InterpretatationMinimizing gaps at the stem-cement interface and encouraging bony apposition at the cement-bone interface would be clinically desirable. The cement-bone interface does not act as a bonded interface in actual use, even in radiographically well-fixed components. Rather, the interface is quite compliant, with sliding and opening motions between the cement and bone surfaces.
Aseptic loosening of cemented tibial components in total knee arthroplasty (TKA) has been related to inadequate cement penetration into the trabecular bone bed during implantation. Recent postmortem retrieval work has also shown there is loss of interlock between cement and bone by resorption of trabeculae at the interface. The goal of this study was to determine if TKAs with more initial interlock between cement and bone would maintain more interlock with in vivo service (in the face of resorbing trabeculae) and have less micro-motion at the cement–bone interface. The initial (created at surgery) and current (after in vivo service) cement–bone interlock morphologies of sagittal implant sections from postmortem retrieved tibial tray constructs were measured. The implant sections were then functionally loaded in compression and the micro-motion across the cement–bone interface was quantified. Implant sections with less initial interdigitation between cement and bone and more time in service had less current cement–bone interdigitation (r2 = 0.86, p = 0.0002). Implant sections with greater initial interdigitation also had less micro-motion after in vivo service (r2 = 0.36, p = 0.0062). This work provides direct evidence that greater initial interlock between cement and bone in tibial components of TKA results in more stable constructs with less micro-motion with in vivo service.
Axial torsional loads representative of gait and stair climbing conditions were applied to transverse sections of 8 uncemented postmortem retrievals and a high-resolution imaging system with digital image correlation was used to measure local micromotion along the bone-implant interface. For seven components that were radiographically stable, there was limited micromotion for gait loading (1.42±1.33 μm) that increased significantly (p=0.0032) for stair climb loading (7.32±9.96 μm). A radiographically loose component had motions on the order of 2.3 mm with gait loading. There was a strong inverse relationship between the amount of bone-implant contact (contact fraction) (p=0.001) and micromotion. The uncemented components had greater contact fraction (41.8±14.4% vs. 11.5±10.2%, p=0.0033) and less median micromotion (0.81±0.79μm vs. 28.8±51.1μm) compared to a previously reported study of cemented retrievals.
The mechanical loads acting across the knee joint following total knee replacements (TKR) during activities of daily living have recently been measured using instrumented TKRs. Using a series of postmortem retrieved TKR constructs we investigated whether these mechanical loads could result in damage to the implant bone interface or supporting bone in the tibia. Eighteen cemented en bloc tibial components (0 to 22 years in service) were loaded under axial compression in increments from 1 to 10 times body weight and digital image correlation was used to measure bone strain and interface micromotion during loading and unloading. Failure was considered to occur when micromotion exceeded 150 μm or compressive bone strain exceeded 7300 με. The results show that all retrieved specimens had sufficient bone strength to support most activities of daily living, but ~40% would be at risk under larger physiologic loads that might occur secondary to a higher impacts such as jogging or a stumble. The tray-bone micromotion (regression model R2=0.48, p=0.025) was greater for donors with lower age at implantation (p=0.0092). Proximal bone strain (model R2=0.46, p=0.03) was greater for donors with longer time in service (p=0.021). Distal bone strain (model R2=0.58, p=0.005) was greater for donors with more time in service (p=0.0054) and lower peri-implant BMD (p=0.049). High mechanical overload of a single or repetitive nature may be an initiating factor in aseptic loosening of total joint arthroplasties and should be avoided in order to prolong the life of the implant.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.