To compare the color stability of Cention N, Fuji IX GP Extra, and Fuji IX GP after thermocycling. Material and Methods: Ten discs of each material of dimension 10 x 1 mm were prepared using a split mold. The preparations of the specimens were done according to the powder/liquid ratio as recommended by the manufacturers [4.6:1, 3.4:1 and 3.6:1 for the groups I, II, and III, respectively]. After setting, the samples were retrieved, and the thickness of each specimen was measured using a micrometer at five different locations. The specimens with variations in thickness, porosity or cracks were discarded and thus not included in the study. The selected specimens were stored in distilled water for 24 hours prior to testing. The prepared specimens were thermocycled at 5°C and 55°C, with a dwell time of 15 seconds for 250 or 500 cycles. Subsequently, the color parameters of the discs were measured using a spectrophotometer. The data were analyzed using two way ANOVA test, and a p-value <0.001 was considered. Results: Thermocycling resulted in changes in the color of both Glass Ionomer cement and Cention N (p<0.001). Among the materials tested, Cention N showed superior color stability. Conclusion: Cention N exhibited better color stability compared to Glass ionomer cements.
Objective: To evaluate and compare the effect of 17% Ethylenediaminetetraacetic Acid (EDTA), 9% Etidronic acid (HEDP), and 7% Maleic acid (MA) on the push-out bond strength of NeoMTA Plus sealer to the coronal, middle, and apical thirds of root canal dentin. Material and Methods: Forty single-rooted human maxillary central incisors were selected and decoronated to 12 mm long root fragments. Working length was established and root canals were then enlarged up to rotary Protaper F3. After each instrumentation, the root canal was irrigated with 2.5% NaOCl. For the final irrigation regimen, the specimens were divided into 4 groups (n=10) and treated with EDTA, HEDP, MA or Saline. Root canals were coated with NeoMTA Plus sealer, and obturation was done with single cone obturation technique. Subsequently, three horizontal sections were taken from the coronal, middle and apical thirds of each specimen, and POBS was measured using a universal testing machine. The type of bond failures was assessed under a stereomicroscope. Statistical analysis was done with One-way ANOVA with Tukey's Post hoc analysis. Results: MA and EDTA showed the highest POBS. There was no significant difference in bond strength between MA and EDTA (p>0.05). HEDP and Saline showed lower POBS. Among all the four groups, the coronal third showed the highest values, followed by middle and apical thirds.
Conclusion:The type of chelating agent used during the root canal treatment significantly affects the bond strength of NeoMTA Plus to the root canal dentin.
A case of peg-shaped lateral with dens invaginatus (DI) and midline diastema affecting maxillary incisors in a 32-year old female patient is discussed. This clinical report describes the endodontic management of DI in tooth #12, esthetic correction of peg laterals and diastema with all ceramic restorations. Satisfactory results were achieved esthetically following treatment and gave the patient a new confident smile.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.