PURPOSEThis in vitro study investigated and compared the durability and retention of three types of attachments.MATERIALS AND METHODSThree commercially available attachments were investigated: Clix®, Dalbo-Plus® and Locator®. In total, 72 samples of these attachments were placed in the acrylic resin forms and subjected to mechanical testing (5400 cycles of insertion and removal) over the respective ball or Locator abutments immersed in artificial saliva at pH 7 and 37℃. The abutments were placed at angulations of 0°, 10° and 20°. The retention force was recorded at the beginning and after 540, 1080, 2160, 3240, 4320 and 5400 insertion-removal cycles.RESULTSThe results revealed that there were significant differences in the average values of the insertion/removal force due to angulation (F (2.48) = 343619, P<.05) and the type of attachment (F (7.48) = 23.220, P<.05).CONCLUSIONGreater angulation of the abutments was found to influence the retention capacity of the attachments, and the fatigue test simulating 5 years of denture insertion and removal did not produce wear in the metal abutments.

PURPOSEThe aim of this study was to compare the durability and retention of 4 types of attachments placed over computer aided design/computer aided manufacturing (CAD/CAM) titanium bars when subjected to different pH conditions.MATERIALS AND METHODSFour commercially available attachments were investigated: Hader Yellow, Hader Red, Ackerman Gold and Ackerman Stainless Steel. These attachments and Ackerman CAD/CAM titanium bars were placed in 2 vessels containing different artificial saliva solutions (pH 7/pH 4) at 37℃ for one month to simulate corrosion conditions, and they were then subjected to mechanical testing (5400 cycles of insertion and removal).RESULTSThe results revealed that there were significant differences in the average values of insertion/removal force due to the pH (F (1, 24)=9.207, P<.05) and the type of attachment (F (3, 24)=11.742, P<.05).CONCLUSIONMore acidic pH values were found to have a negative influence on the retention capacity of the attachments.

Topographical features of biomaterials' surfaces are determinant when addressing their application site. Unfortunately up to date there has not been an agreement regarding which surface parameters are more representative in discriminating between materials. Discs (n = 16) of different currently used materials for implant prostheses fabrication, such as cast cobalt-chrome, direct laser metal soldered (DLMS) cobalt-chrome, titanium grade V, zirconia (Y-TZP), E-glass fiber-reinforced composite and polyetheretherketone (PEEK) were manufactured. Nanoscale topographical surface roughness parameters generated by atomic force microscopy (AFM), microscale surface roughness parameters obtained by white light interferometry (WLI) and water angle values obtained by the sessile-water-drop method were analyzed in order to assess which parameter provides the best optimum surface characterization method. Correlations between nanoroughness, microroughness, and hydrophobicity data were performed to achieve the best parameters giving the highest discriminatory power. A subset of six parameters for surface characterization were proposed. AFM and WLI techniques gave complementary information. Wettability did not correlate with any of the nanoroughness parameters while it however showed a weak correlation with microroughness parameters.

No abstract

No abstract