In the present investigation synthesis, microstructure, mechanical and wear behavior of 5 weight percentage of nano Al2O3 particulate reinforced AA7475 alloy composites has been reported. AA7475 matrix composite containing nano Al2O3 were fabricated by conventional stir casting method. The microstructures of the composites were examined by scanning electron microscopy. Further, mechanical and wear behavior of as cast AA7475 alloy and AA7475 - 5 wt. % nano Al2O3 composites were studied. Mechanical properties like hardness, ultimate, yield strength and percentage elongation were evaluated as per ASTM standards. Pin on disc apparatus was used to conduct the dry sliding wear tests. The experiments were conducted by varying loads and constant sliding speed of 300rpm for sliding distance of 4000m. Microstructural observation revealed the uniform distribution of particles in the AA7475 alloy matrix. From the analysis, it was found that the hardness, ultimate tensile strength and yield strength of composites were increased due to addition of nano Al2O3 particle in the AA7475 alloy matrix. Percentage elongation of the composite decreased in 5 wt. % nano Al2O3 reinforced composites. Further, the volumetric wear loss was found to increase with the load and sliding distance for all materials. Worn surface analysis made by using scanning electron micrographs to know the various mechanisms involved in the wear process.

No abstract

No abstract

Aluminum boron carbide metal matrix composites (Al-MMC) have got wide applications in aeronautical and automobile industries due to their excellent mechanical and physical properties. Due to the presence of harder reinforcement particles, machining of these composites is a difficult task. The results of experimental investigation on mechanical and machinability properties of Boron carbide particle (B4Cp) reinforced aluminum metal matrix composites are presented in this paper.The influence of reinforced ratio of 7 wt% of B4Cpon mechanical properties was examined. It was observed that addition of B4Cpreinforcement resulted in improvement in hardness and tensile strengths to the extent of 71% and 38.4% respectively. Fabricated samples were turned on medium duty lathe of 3 kW spidle power with Poly crystalline diamond tool (PCD) of 10 μm particle size at various cutting conditions. The effect of machining parameters, e.g. cutting speed, feed rate and depth of cut on cutting forces and formation of BUE was studied.

No abstract