Numerous papers and publications report the use of microporous calcium hexaluminate (CaO.6Al 2 O 3 ; CA 6 ) as a key raw material for high temperature insulating materials. This material has unique properties with respect to chemical purity and mineral composition. Another important property of CA 6 is its structure, which consists of platelet-shaped crystals that interlock. The free distance between the crystals defines the microporous structure. The low density in combination with the micropores hampers heat transfer by radiation at temperatures exceeding 1000 o C and results in a low thermal conductivity. Given the advantages presented by this material, it is necessary to understand the formation mechanism of CA 6 grains in order to better develop the potential applications of this material. CA 6 can be fabricated using organic binders to consolidate the Al 2 O 3 -CaCO 3 powder mixture and to provide green strength so that a green body can be formed and retains the desired shape before heating. However, these organic binders must be completely thermally decomposed so that they do not remain in the sintered body as carbon or ash. Moreover, the use of organic binders releases large volumes of gases such as carbon dioxide from the green body during heating. Therefore, an eco-friendly ceramic fabrication process has been developed that employs an inorganic binder (hydraulic alumina). The aim of the present work was to study the synthesis of porous calcium-hexaluminate ceramics using calcined alumina or hydraulic alumina combined with different sources of calcia (CaCO 3 and Ca(OH) 2 ) at different temperatures. The materials produced were characterized by X-ray diffraction, scanning electron microscopy, apparent porosity and mercury intrusion porosimetry. The materials produced by hydraulic alumina presented higher porosity and larger pores compared to those produced from calcined alumina.

Direitos para esta edição cedidos à Atena Editora pelos autores. Todo o conteúdo deste livro está licenciado sob uma Licença de Atribuição Creative Commons. Atribuição-Não-Comercial-NãoDerivativos 4.0 Internacional (CC BY-NC-ND 4.0).O conteúdo dos artigos e seus dados em sua forma, correção e confiabilidade são de responsabilidade exclusiva dos autores, inclusive não representam necessariamente a posição oficial da Atena Editora. Permitido o download da obra e o compartilhamento desde que sejam atribuídos créditos aos autores, mas sem a possibilidade de alterá-la de nenhuma forma ou utilizá-la para fins comerciais. Todos os manuscritos foram previamente submetidos à avaliação cega pelos pares, membros do Conselho Editorial desta Editora, tendo sido aprovados para a publicação com base em critérios de neutralidade e imparcialidade acadêmica.A Atena Editora é comprometida em garantir a integridade editorial em todas as etapas do processo de publicação, evitando plágio, dados ou resultados fraudulentos e impedindo que interesses financeiros comprometam os padrões éticos da publicação. Situações suspeitas de má conduta científica serão investigadas sob o mais alto padrão de rigor acadêmico e ético.