A selective wet etching process for fabricating SiGe and Ge nanowires for gate all around transistors is introduced in this paper. Two formulated proprietary chemical mixtures with highly selective etching properties (Si vs. SiGe and SiGe vs. Ge) can effectively dissolve the sacrificial layers with minimal damage to the interstitial nanowire materials. The Auger Electron Spectroscopy (AES) surface characterization indicates that no chemical contamination is left after the wet etching process.

Gate All-Around (GAA) is considered a key design feature for future CMOS technology. SiGe vs. Si selective etch is required for Si nanowire formation in GAA. It is confirmed the selective SiGe removal with commodity chemical (mixtures of hydrofluoric acid (HF), hydrogen peroxide (H2O2) and acetic acid (CH3COOH, HAc)), however the thick oxidized layer on Si NW was observed after commodity chemical process, which is indicated the significant Si NW loss. On the other hand, the formulated mixture ACT® SG-101, which is focusing on SiGe oxidizer, chemical pH, solvent polarity & corrosion inhibitor for chemical concept, was performed higher selectivity and lower Si loss than commodity chemical. The formulated mixture has also been used to form an inner spacer for cavity etch scheme and confirmed uniform cavity etch and inner spacer filling on topological test structure.