To explore the influence of different factors on the shear resistance of the fiber-reinforced Engineered Cementitious Composite (ECC) and ordinary concrete interface, the influence rule of rib width, rib height, and planting bars ratio on the interface shear strength of steel fiber-reinforced ECC and ordinary concrete was investigated by orthogonal experimental design. The experimental results show the rib width is the most important factor affecting the shear strength of the interface, and the ratio of planting bars minimally influences the shear strength of the interface. The order of main influence factors of shear resistance of interface can be arranged as follows: rib width→rib height→planting bars ratio. Experimental process and load-displacement curve show the failure of the double-sided shear specimen with ribs or planting bars has certain plastic failure characteristics, which extends the failure time of the specimens.

The impregnated diamond composites are widely used for rock drilling and the processing of construction materials. In order to decrease the sintering temperature so as to reduce the thermal damage of diamond, and ultimately improve the sharpness of the diamond tool, the iron-nickel pre-alloyed powder sintered specimens and the impregnated diamond composites were prepared by powder metallurgy. The microstructure and phase composition of specimens were characterized by SEM and EDS. The effect of sintering temperature and the content of WC particles on the mechanical properties of the specimens, such as relative density, hardness, bending strength and wear resistance were investigated. The results showed that the relative density, hardness and bending strength of the sintered specimens increased first and then decreased with the sintering temperature changing from 700 °C to 900 °C. The performance of the specimens sintered at 800 °C was the best, with the corresponding values of 97.75%, 24.0 HRC and 2114.87 MPa. The optimum content of WC was 30wt%, and the grinding ratio reached to 424.11. The rate of penetration of drilling bits with iron-nickel pre-alloyed based matrix increased by 91.14% compared with the traditional bits which used 663Cu-Co-Ni-Mn as binder.