Inexpensive raw materials have been used to prepare ZSM-5 zeolites with SiO2/Al2O3 molar ratios in the range 20 – 40. Kaolin or Bolivian diatomaceous earth was used as aluminosilicate raw materials and sodium hydroxide and n-butylamine were used as mineralizing agents and template. Dealumination of the raw materials by acid leaching made it possible to reach appropriate SiO2/Al2O3 ratios and to reduce the amount of iron and other impurities. After mixing the components and aging, hydrothermal treatment was carried out and the products were recovered The results clearly show for the first time that well-crystallized ZSM-5 can be directly prepared from leached metakaolin or leached diatomaceous earth using sodium hydroxide and n-butylamine as mineralizing agents and template under appropriate synthesis conditions. A longer induction time prior to crystallization was observed for reaction mixtures prepared from leached diatomaceous earth, probably due to slower digestion of the fossilized diatom skeletons as compared with that for microporous leached metakaolin. The use of leached diatomaceous earth allowed higher yield of ZSM-5 crystals within comparable synthesis times. However, low amounts of Mordenite formed, which was related to the high calcium content of diatomaceous earth. Another considerable advantage of diatomaceous earth over kaolin is that diatomaceous earth does not require heat treatment at high temperature for metakaolinization.

Porous gel structures are formed during the synthesis of the zeolite ZSM-5 due to the reaction between a source of aluminosilicate, sodium hydroxide, water and a structure directing agent, such as e.g. tetrapropylammonium (TPA) or n-butylamine (NBA). In the present work, the formation of the gel in a heterogeneous system leading to the crystallization of NBA-ZSM-5 zeolite from leached metakaolin was studied extensively. The solid and liquid phases obtained after separation were analyzed by inductively coupled plasma sector field mass spectrometry, dynamic light scattering, extreme high resolution-scanning electron microscopy, energy dispersive spectroscopy, high resolution-transmission electron microscopy, X-ray diffraction and nitrogen gas adsorption. The main gel phase formed after hydrothermal treatment exhibited a sponge-like structure resembling those forming in (Na, TPA)-ZSM-5-based systems. For the first time, the walls of the main gel were shown to be inhomogenous and to possess a biphasic internal structure consisting of a mesoporous skeleton of aluminosilicate nanoparticles embedded in a silicate-rich soluble matrix of soft matter. The data presented in this paper is of primary importance to understand the mechanism by which the gel is consumed and contributes to the growth process of the zeolite crystals.